激光工艺参数对NiCoCrAlYSi熔覆层微观组织及性能的影响

doi:10.3969/j.issn.1000-1093.2021.07.020

摘要/Abstract

摘要： 采用激光熔覆技术在Ni625高温合金表面制备NiCoCrAlYSi涂层，研究激光功率和扫描速度对NiCoCrAlYSi熔覆层冶金质量及微观组织的影响。通过测试熔覆层显微硬度及摩擦磨损性能，建立激光熔覆工艺参数、微观组织与熔覆层性能之间的关系。结果表明：随着激光输入能量从36 J/mm²升高至73.3 J/mm²，熔覆层厚度从534 μm增加到1 535 μm，表面气孔率从0.07%增大到0.65%，以及平均气孔尺寸从0.23 μm增大到1.33 μm，且熔覆层微观组织发生粗化，熔覆层表面气孔率的增大及组织粗化导致其显微硬度和耐磨性逐渐降低；当激光输入能量比为36 J/mm²时，熔覆层组织致密性最高、晶粒尺寸最细小，且内部分布有大量的位错及位错墙结构，此时熔覆层硬度及耐磨性也最佳。

关键词: Ni625高温合金, 激光熔覆, 扫描速度, 激光功率, 微观组织, 显微硬度, 摩擦磨损性能

Abstract: NiCoCrAlYSi coating was fabricated on Ni625 superalloy by laser cladding technique, and the influences of laser power and scanning speed on the metallurgical quality and microstructure of NiCoCrAlYSi cladding coating were researched. The relationship among the laser cladding process parameters, and the microstructures and properties of cladding coating was analyzed by testing its micro-hardness, and friction and wear properties. The results show that, with the increase in laser input energy from 36 J/mm² to 73.3 J/mm², the thickness of cladding layer increases from 534 μm to 1 535 μm, the surface porosity increases from 0.07% to 0.65%, and the pore size increases from 0.23 μm to 1.33 μm. In addition, the grain size of cladding layer increases. The microhardness and wear resistance of the cladding layer decrease gradually with the increase in porosity and grain size. When the laser input energy ratio is 36 J/mm², a cladding coating with high compactness, supper refined grains and high density of dislocations is obtained, which has optimal microhardness and wear resistance.

Key words: Ni625superalloy, lasercladding, scanningspeed, laserpower, microstructure, microhardness, frictionandwearproperty

中图分类号:

TG174.442⁺.9

沈浩，蔡杰，吕鹏，张从林，李玉新，关庆丰. 激光工艺参数对NiCoCrAlYSi熔覆层微观组织及性能的影响[J]. 兵工学报, 2021, 42(7): 1524-1534.

SHEN Hao, CAI Jie, L Peng, ZHANG Conglin, LI Yuxin, GUAN Qingfeng. Effect of Laser Process Parameters on Microstructures and Properties of NiCoCrAlYSi Laser Cladding Coating[J]. Acta Armamentarii, 2021, 42(7): 1524-1534.

参考文献

［1］郭洪波, 宫声凯, 徐惠彬. 新型高温/超高温热障涂层及制备技术研究进展［J］. 航空学报, 2014, 35(10): 2722-2732.
GUO H B, GONG S K, XU H B. Research progress on new high/ultra-high temperature thermal barrier coatings and progressing technologies［J］. Acta Aeronautica et Astronautica Sinica, 2014, 35(10): 2722-2732. (in Chinese)
［2］刘勇, 刘赛月, 王铀, 等. 面向高端装备关键构件的纳米热喷涂涂层［J］. 材料导报, 2016, 30(增刊1): 67-72.
LIU Y, LIU S Y, WANG Y, et al. Nano thermal spraying coating facing key components in high-side equipment［J］. Materials Review, 2016, 30(S1): 67-72. (in Chinese)
［3］崔耀欣, 汪超, 何磊,等. 重型燃气轮机先进热障涂层研究进展［J］. 航空动力, 2019(2):66-69.
CUI Y X, WANG C, HE L, et al. The development of advanced TBC for heavy duty gas turbines［J］. Aerospace Power, 2019(2):66-69.(in Chinese)
［4］ PADTURE N P, GELL M, JORDAN E H. Thermal barrier coatings for gas-turbine engine applications［J］. Science, 2002, 296(5566): 280-284.
［5］余春堂,阳颖飞,鲍泽斌, 等. 先进高温热障涂层用高性能粘接层制备及研究进展［J］. 中国腐蚀与防护学报, 2019, 39(5): 395-403.
YU C T, YANG Y F, BAO Z B, et al. Research progress in pre-paration and development of excellent bond coats for advanced thermal barrier coatings［J］. Journal of Chinese Society for Corrosion and Protection, 2019, 39(5): 395-403.(in Chinese)
［6］ POMEROY M J. Coatings for gas turbine materials and long term stability issues［J］. Materials & Design, 2005, 26(3): 223-231.
［7］梁静静, 韦华, 侯桂臣, 等. 高温涂层材料物理、力学性能研究进展［J］. 稀有金属材料与工程, 2008, 37(7): 1134-1138.
LIANG J J, WEI H, HOU G C, et al. Progress in mechanical and physical properties of high-temperature coating materials［J］. Rare Metal Materials and Engineering, 2008, 37(7): 1134-1138. (in Chinese)
［8］王东生, 田宗军, 沈理达, 等. 激光熔覆MCrAlY涂层的研究现状［J］. 机械工程材料, 2013, 37(12): 1-5.
WANG D S, TIAN Z J, SHEN L D, et al. Research status of MCrAIY coatings prepared by laser cladding［J］. Materials for Mechanical Engineering, 2013, 37(12): 1-5. (in Chinese)
［9］ TOBAR M J, AMADO J M, YEZ A, et al. Laser cladding of MCrAlY coatings on stainless steel［J］. Physics Procedia, 2014, 56(8): 276-283.
［10］ SEO J W, KIM J, KWON S J, et al. Effects of laser cladding for repairing and improving wear of rails［J］. International Journal of Precision Engineering and Manufacturing, 2019, 20(7): 1207-1217.
［11］徐婷, 李华兵, 洪翔, 等. 激光熔覆TiB₂颗粒增强镍基合金复合涂层的微观组织与摩擦学性能研究［J］.兵工学报, 2016, 37(8): 1497-1505.
XU T, LI H B, HONG X, et al. Microstructure and tribological properties of laser cladding TiB₂/Ni-based alloy composite coatings［J］. Acta Armamentarii, 2016, 37(8): 1497-1505. (in Chinese)
［12］郭纯, 陈建敏, 姚润钢, 等. 激光熔覆NiCoCrAlY/ZrB2复合涂层结构及高温耐磨性能［J］. 稀有金属材料与工程, 2013, 42(8): 1547-1551.
GUO C, CHEN J M, YAO R G, et al. Microstructure and high temperature wear resistance of laser cladding NiCoCrAlY/ZrB2 coating［J］. Rare Metal Materials and Engineering, 2013, 42(8): 1547-1551. (in Chinese)
［13］ TABERNERO I, LAMIKIZ A, MARTNEZ S, et al. Evaluation of the mechanical properties of Inconel 718 components built by laser cladding［J］. International Journal of Machine Tools & Manufacture, 2011, 51(6): 465-470.
［14］练国富, 姚明浦, 陈昌荣,等. 激光熔覆多道搭接成形质量与效率控制方法［J］. 表面技术, 2018, 47(9): 229-239.
LIAN G F, YAO M P, CHEN C R, et al. Control of the quality and efficiency of multi-track overlapping laser cladding［J］. Surface Technology, 2018, 47(9): 229-239. (in Chinese)
［15］ ZHANG Y, TENG F H, XIAO M, et al. Effect of process parameters on the microstructure and properties of laser-clad FeNiCoCrTi0.5 high-entropy alloy coating［J］. International Journal of Minerals Metallurgy and Materials, 2020, 27(5): 630-639.
［16］ EMAMIAN A, CORBIN S F, KHAJEPOUR A. Effect of laser cladding process parameters on clad quality and in-situ formed microstructure of Fe-TiC composite coatings［J］. Surface & Coatings Technology, 2010, 205(7): 2007-2015.
［17］ ZHOU C Y, ZHAO S S, WANG Y B, et al. Mitigation of pores generation at overlapping zone during laser cladding［J］. Journal of Materials Processing Technology, 2015, 216: 369-374.
［18］ ERFANMANESH M, ABDOLLAH-POUR H, MOHAMMADIAN-SEMNANI H, et al. An empirical-statistical model for laser cladding of WC-12Co powder on AISI 321 stainless steel［J］. Optics & Laser Technology, 2017, 97: 180-186.
［19］ WENG Z K, WANG A H, XIONG D H, et al. Diode laser cladding of Fe-based alloy on ductile cast iron and related interfacial behavior［J］. Surface & Coatings Technology, 2016, 286: 64-71.
［20］赵尧, 虞钢, 何秀丽, 等. 基于主成分分析法与逼近理想解法的38MnVS6激光熔覆工艺研究［J］. 兵工学报, 2019, 40(12): 2537-2544.
ZHAO R, YU G, HE X L, et al. Research on laser cladding processing for 38MnVS6 by PCA-TOPSIS Method［J］. Acta Armamentarii, 2019, 40(12): 2537-2544. (in Chinese)
［21］童文辉, 张新元, 李为轩, 等. 激光工艺参数对TiC增强钴基合金激光熔覆层组织及性能的影响［J］. 金属学报, 2020, 56(9): 1265-1274.
TONG W H, ZHANG X Y, LI W X, et al. Effect of laser process parameters on the microstructure and properties of TiC reinforced Co-based alloy laser cladding layer［J］. Acta Metallurgica Sinica, 2020, 56(9): 1265-1274. (in Chinese)
［22］ LUO G Y, XIAO H, LI S M, et al. Quasi-continuous-wave laser surface melting of aluminium alloy: precipitate morphology, solute segregation and corrosion resistance［J］. Corrosion Science, 2019, 152: 109-119.
［23］ ZHANG N, LIU W W, DENG D W, et al. Effect of electric-magnetic compound field on the pore distribution in laser cladding process［J］. Optics & Laser Technology, 2018, 108: 247-254.
［24］ ZHONG C L, GASSER A, KITTEL J, et al. Improvement of material performance of Inconel 718 formed by high deposition-rate laser metal deposition［J］. Materials & Design, 2016, 98: 128-134.
［25］ CAI J G, YANG S Z, JI L, et al. Surface microstructure and high temperature oxidation resistance of thermal sprayed CoCrAlY coating irradiated by high current pulsed electron beam［J］. Surface and Coatings Technology, 2014, 251: 217-225.
［26］ CAI J, GUAN Q F, HOU X L, et al. Isothermal oxidation behaviour of thermal barrier coatings with CoCrAlY bond coat irradiated by high-current pulsed electron beam［J］. Applied Surface Science, 2014, 317: 360-369.
［27］关庆丰, 顾倩倩, 李艳, 等. 强流脉冲电子束作用下金属纯Cu的微观结构状态-变形结构［J］. 物理学报, 2011, 60(8): 508-514.
GUAN Q F, GU Q Q, LI Y, et al. Microstructures in polycrystalline pure copper induced by high-current pulsed electron beam-deformation structures［J］. Acta Physica Sinica, 2011, 60(8): 508-514. (in Chinese)
［28］程笃庆, 关庆丰, 朱健, 等.强流脉冲电子束诱发纯镍表层纳米结构的形成机制［J］. 物理学报, 2009, 58(10): 7300-7306.
CHENG D Q, GUAN Q F, ZHU J, et al. Mechanism of surface nanocrystallization in pure nickel induced by high-current pulsed electron beam［J］. Acta Physica Sinica, 2009, 58(10):7300-7306. (in Chinese)
［29］ JEYAPRAKASH N, YANG C H, RAMKUMAR K R. Microstructure and wear resistance of laser cladded Inconel 625 and Colmonoy 6 depositions on Inconel 625 substrate［J］. Applied Physics A, 2020, 126(6):455.
［30］ GUO C, ZHOU J S, CHEN J M, et al. High temperature wear resistance of laser cladding NiCrBSi and NiCrBSi/WC-Ni composite coatings［J］. Wear, 2011, 270(7/8): 492-498.
［31］ JEYAPRAKASH N, YANG C H, DURAISELVAM M, et al. Microstructure and tribological evolution during laser alloying WC-12%Co and Cr₃C₂25%NiCr powders on nodular iron surface［J］. Results in Physics, 2019, 12:1610-1620.

[1]	宁子轩，王琳，程兴旺，程焕武，周哲，张斌斌，王芳，陈东萍. 微观组织对Ti6321钛合金靶板爆炸断裂失效的影响[J]. 兵工学报, 2021, 42(7): 1506-1515.
[2]	马良超, 王大锋, 马冰, 陈东高, 张迎迎. 不同氮含量焊丝熔化极气体保护焊高氮钢的微观组织与力学性能[J]. 兵工学报, 2021, 42(6): 1303-1311.
[3]	聂金浩，杨宜鑫，李玉新，张宏建，魏守征，蔡杰，关庆丰. 激光能量密度对激光熔覆NiCoCrAlY涂层组织与性能的影响[J]. 兵工学报, 2021, 42(5): 1083-1091.
[4]	李昌，于志斌，高敬翔，李云飞，韩兴. 物性参数温度变化下激光熔覆多场耦合模拟与实验[J]. 兵工学报, 2019, 40(6): 1258-1270.
[5]	赵尧，虞钢，何秀丽，李海明，李少霞. 基于主成分分析法与逼近理想解法的38MnVS6激光熔覆工艺研究[J]. 兵工学报, 2019, 40(12): 2537-2544.
[6]	石岩，刘东炜，刘佳，李凌宇. 硬脆钢50SiMnVB激光预控裂纹工艺试验研究[J]. 兵工学报, 2018, 39(10): 1997-2005.
[7]	赵丹丹，焦锋. 基于灰色关联分析的35CrMoV钢活塞杆激光熔覆工艺参数优化[J]. 兵工学报, 2018, 39(10): 2073-2080.
[8]	梁志强，黄迪青，周天丰，李宏伟，乔治，王西彬，刘心藜. 齿轮钢18Cr2Ni4WA磨削烧伤实验及仿真预测研究[J]. 兵工学报, 2017, 38(10): 1995-2001.
[9]	徐婷，李华兵，洪翔，张中威，林炎炎. 激光熔覆TiB₂颗粒增强镍基合金复合涂层的微观组织与摩擦学性能研究[J]. 兵工学报, 2016, 37(8): 1497-1505.
[10]	胡勇，饶丽，邹天平. 等温热处理对AM60-1Si合金半固态组织的影响[J]. 兵工学报, 2016, 37(4): 690-695.
[11]	李萍，章凯，薛克敏，王晓溪. 新型药型罩温压扭成形模拟与实验研究[J]. 兵工学报, 2012, 33(4): 437-442.
[12]	石岩，张宏，徐春鹰. 激光熔覆科尔莫落依合金涂层的奥氏体不锈钢表面组织和耐磨性研究[J]. 兵工学报, 2010, 31(7): 927-932.
[13]	骆芳，陈智君，楼程华，柴国钟. 塑料模具钢表面激光熔覆陶瓷复合涂层的性能研究[J]. 兵工学报, 2010, 31(7): 933-938.
[14]	石岩，刘佳，张宏，刘双宇. 30CrMnSi钢激光焊接工艺研究[J]. 兵工学报, 2010, 31(7): 991-997.
[15]	杨勇彪，王富耻，谭成文，吴园园，才鸿年. 不同取样方向AZ31B镁合金应变率效应[J]. 兵工学报, 2008, 29(11): 1347-1351.