大口径机枪枪管失效规律研究

doi:10.3969/j.issn.1000-1093.2015.12.004

摘要/Abstract

摘要： 为了研究大口径枪管在寿命过程中的变化规律，寻找失效原因，对两根不同材料枪管进行了综合寿命试验。分析了内膛阳线直径变化、内膛表面形貌变化、密集度、初速下降率及椭圆弹孔率与枪管寿命之间的关系，得到了某机枪两种寿命相差3 000发的寿终枪管的共同规律为：枪管寿终均表现为椭圆弹孔率超过本组射弹量的50%，内膛四锥、五锥的损伤是造成枪管产生椭圆弹孔的根本原因；在射弹量为1 200发时，枪管内膛五锥处的铬层已经严重成片脱落；由于枪管内膛尾部出现了鼓形，用量规测量得到的枪管内膛直径大小并不能反应枪管性能，但尾部阳线直径变化越快，枪管寿命越短。

关键词: 兵器科学与技术, 枪管, 寿命试验, 内膛, 寿命, 损伤

Abstract: In order to study the erosion rule of large caliber machinegun barrel in lifetime and find out the determinants of barrel life, the life test was done on two barrels made of different materials. The fundamental cause of the ellipse shot holes due to the erosion of the forth and fifth tapers are found out by analyzing the relations among the barrel life and the changes of bore land diameter and bore surface topography, accuracy and dispersion, decreased rate of muzzle velocity and number of ellipse shot holes, which results in the different life of two barrels; when firing 1 200 shots, the chrome layer in the fifth taper of bore fell off, the bore diameter measured by gauge can’t reflect barrel performance, but the barrel life is determinated by the changing of land diameter in the rear of barrel.

Key words: ordnance science and technology, barrel, life test, bore, life, erosion

中图分类号:

TJ10

乔自平，李峻松，薛钧. 大口径机枪枪管失效规律研究[J]. 兵工学报, 2015, 36(12): 2231-2240.

QIAO Zi-ping， LI Jun-song， XUE Jun. Research on the Performance Decay Rule of Large Caliber Machinegun Barrel[J]. Acta Armamentarii, 2015, 36(12): 2231-2240.

参考文献

［1］游首先, 丁志洪, 王立，等. 兵器工业科学技术辞典[M]. 北京：国防工业出版社，1998：5-56.
YOU Shou-xian，DING Zhi-hong，WANG Li，et al. Dictionary of ordnance industry science and technology [M]. Beijing：National Defense Industry Press，1998：5-56. (in Chinese)
[2] Kim J B. Combined effects of a gun profile and sabot on the strength of penetrator [J]. International Journal of Modern Physics, 2006, 20(5): 4517-4522.
[3] Chung D Y, Shin N, Oh M，et al. Prediction of erosion from heat transfer measurements of 40mm gun tubes [J]. Wear, 2007, 263(1)： 246-250.
[4] 吴斌，夏伟，汤勇，等.射击过程中热影响及身管热控制措施综述[J]. 兵工学报，2003，24(4)：525-529.
WU Bin，XIA Wei，TANG Yong，et al. A review on thermal effects during the firing process and measures of their thermal control[J]. Acta Armamentarii，2003，24(4)：525-529.（in Chinese）
[5] 樊磊, 刘恩锦, 刘卫明, 等. 大口径机枪枪管寿命趋势分析[J].弹道学报, 2009, 21(3): 39-43.
FAN Lei，LIU En-jin，LIU Wei-ming，et al. Performance decay analysis of a large caliber machine gun barrel in lifetime [J]. Journal of Ballistics, 2009, 21(3): 39-43.（in Chinese）
[6] Mishra A, Hameed A, Lawton B. Transient thermal analyses of midwall cooling and external cooling methods for a gun barrel [J]. Heat Transfer, 2010, 132(9): 091901-8.
[7] 单永海，张军，王全正，等. 机枪身管常温综合寿命试验技术研究[J]. 兵工学报，2013，34(1)：1-7.
SHAN Yong-hai，ZHANG Jun，WANG Quan-zheng，et al. Study on lifetime test for machinegun barrel in normal temperature[J]. Acta Armamentarii，2013，34(1)：1-7.（in Chinese）
[8] 张坤, 胡莹, 陈光南, 等. 身管内膛镀铬层的抗烧蚀性能研究 [C]∥ 全国第五届航空航天装备失效分析研讨会.宁波：宇航学会，2007: 395-399.
ZHANG Kun，HU Ying，CHEN Guang-nan，et al. The chromium plating layer bore the ablation resistance of research[C]∥ The Fifth National Aerospace Equipment Failure Analysis Seminar. Ningbo：Chinese Society of Astronautics，2007: 395-399. （in Chinese）
[9] Lawton B. Simulation of gun barrel erosion in a vented vessel [C]∥ The 11th International Symposium on Ballistics. Brussels,Belgium：AIAA，1989：172-179.
[10] Lawton B. Thermo-chemical erosion in gun barrels [J]. Wear, 2001, 251(10): 827-838.
[11] Lawton B. Simulation of gun barrel erosion in a vented vessel[C]∥ The 11th International Symposium on Ballistics. Brussels,Belgium：AIAA，1989:187-190.
[12] 卓穗如. 机枪枪管寿命预测技术[M].北京：中国兵器工业第208研究所, 1996: 1-15.
ZHUO Sui-ru. Gun barrel life prediction technology[M].Beijing：No 208 Institute of China Ordnance Industry, 1996: 1-15.（in Chinese）
[13] Ahmad I, Stiefel L. The problem of gun barrel erosion [J]. Astronautics and Aeronautics，1988, 109：311-355.
[14] Sopok S. Erosion modeling of vented combustor cannon bore materials[C]∥ The 35th AIAA Thermophysics Conference. Anaheim, California, US：AIAA，2001:156-159.
[15] Andrade C A, Cunningham B, Nagamatsu H T, et al. The cannon-projectile blow-by flow field[C]∥ Chemical Propulsion Information Agency. Cleveland：Army Armament Research Development and Engineering Center Watervliet NY Benet Labs，1998: 125-132.
[16] Underwood J H，Witeherell M D，Sopok S，et al. Thermomechanical modeling of transient thermal damage in cannon bore materials [J]. Wear, 2004, 257（9/10）：992-998.
[17] Lawton B. A new correlation for heat transfer between propellant gas and hot gun barrels[C]∥ The 14th International Symposium on Ballistics. Qébec：AIAA，1993: 87-92.
[18] Chen M M.Projectile balloting attributable to gun tube curvature[J]. Shock and Vibration, 2010, 17(1): 39-53.
[19] Lawton B. Thermal and chemical effects of gun barrel wear[C]∥The 8th International Symposium on Ballistics. Orlando, US：AIAA，1984:58-62.

[1]	张贺，黄毅，刘科言，李朋超，顾桐光，王永娟，徐诚. 盐雾环境对典型步枪自动机运动影响[J]. 兵工学报, 2024, 45(4): 1082-1093.
[2]	徐京, 胡春东, 陆恒昌, 邓亚辉, 薛钧, 韦习成, 董瀚. 枪管用环保镀层摩擦行为研究[J]. 兵工学报, 2024, 45(2): 651-661.
[3]	许耀峰, 杨雕, 刘朋科, 陈奇, 郭俊行, 王军. 火炮身管内膛表面材料强度退化机理研究[J]. 兵工学报, 2023, 44(5): 1288-1295.
[4]	许耀峰, 王军, 刘朋科, 朱文芳, 杨雕. 不同持续射击发数对火炮身管寿命的影响[J]. 兵工学报, 2023, 44(4): 1034-1040.
[5]	毛保全, 赵其进, 白向华, 王之千, 朱锐, 陈春林. 火炮身管延寿技术研究现状与展望[J]. 兵工学报, 2023, 44(3): 638-654.
[6]	王永, 王西彬, 王志斌, 刘志兵, 刘书尧, 陈洪涛, 王湃. 考虑高强度钢加工表面完整性的背应力能法疲劳寿命预测模型[J]. 兵工学报, 2023, 44(3): 806-815.
[7]	李凯, 周诗超, 温鹏, 孙建港, 龚卿青, 李沅, 韩焱. 基于磁散射的线膛炮内表面磨损检测技术[J]. 兵工学报, 2023, 44(3): 748-756.
[8]	牛荣军, 刘越, 唐红利, 崔永存, 邓四二. 多点支撑结构形变及轴系轴承承载性能分析[J]. 兵工学报, 2023, 44(2): 615-628.
[9]	陈子涵. 基于多模态Transformer的机电作动器剩余寿命预测[J]. 兵工学报, 2023, 44(10): 2920-2931.
[10]	雷良，周丹发，张颖，顾村锋，刘瑞. 导弹武器全寿命周期成本分析与控制策略[J]. 兵工学报, 2022, 43(S2): 107-114.
[11]	窦彩虹, 靳鹏飞, 陈俊宇, 汪从珍, 李建军, 张程, 张诚, 黄进峰. 大口径机枪枪管内膛烧蚀行为与微观机理[J]. 兵工学报, 2022, 43(9): 2231-2240.
[12]	周伯俊, 于传强，刘志浩，柯冰. 基于高压储能的特种车辆快速起竖技术与验证[J]. 兵工学报, 2022, 43(7): 1488-1497.
[13]	高月光，冯顺山，刘云辉，黄岐. 不同端盖厚度的圆柱形装药壳体破片初速分布[J]. 兵工学报, 2022, 43(7): 1527-1536.
[14]	刘朋科，杨雕，许耀峰，宁变芳，王军，刘欢. 火炮身管内膛表层温度及其梯度规律研究[J]. 兵工学报, 2022, 43(6): 1225-1232.
[15]	许晓东，唐圣金，谢建，于传强，王凤飞，韩洋洋. 随机退化应力作用下设备剩余寿命预测方法[J]. 兵工学报, 2022, 43(3): 712-719.