关键词: 爆炸力学, 低速贯穿, 组合靶板, 弹道试验, 理论预测

Abstract: Lowvelocity ballistic experiments were carried out to study the perforationresistant mechanisms of warship topside composite armor system, which was simulated by composite laminates at the front and homogeneous steel plates at the back. Failure modes and energy absorbing mechanisms were investigated and the influence of the area density of front composite armors on total perforation resistance of combined targets was analyzed. Based on the experiments, an equation was obtained to predict the residual velocities in the case of lowvelocity perforation of combined targets by hemisphericalnosed projectiles according to the failure modes of the targets. The results show that under low velocity perforation, combined targets mainly exhibit local damage. A few amounts of fiber at the impact side of front composite armor are sheared by the projectile. Failure modes of front composite armors are mainly fiber tensile rupture while for steel backing plates, failure modes are primarily petaloid damage. The whole energyabsorbing capability of combined targets increases with increasing the area density of front composite armors. It is shown that theoretical predictions coincide with the experimental results in terms of residual velocities.

Key words: explosion mechanics, lowvelocity perforation, combined target, ballistic experiment, theoretical prediction