基于内聚裂纹模型的高聚物粘结炸药模拟材料动态断裂行为研究

doi:10.3969/j.issn.1000-1093.2017.12.011

兵工学报 ›› 2017, Vol. 38 ›› Issue (12): 2379-2385.doi: 10.3969/j.issn.1000-1093.2017.12.011

基于内聚裂纹模型的高聚物粘结炸药模拟材料动态断裂行为研究

崔云霄^1，2，陈鹏万¹，郭保桥¹， David A. Cendón³，周忠彬¹

（1.北京理工大学爆炸科学与技术国家重点实验室，北京 100081； 2.西北核技术研究所，陕西西安 710024；3.马德里理工大学，西班牙马德里 28040）

收稿日期:2017-01-10 修回日期:2017-01-10 上线日期:2018-02-01
通讯作者: 陈鹏万（1971—），男，教授，博士生导师 E-mail:pwchen@bit.edu.cn
作者简介:崔云霄（1980—），男，博士研究生。E-mail: yunxiaocui@163.com
基金资助:
国家自然科学基金项目（11202027、11521062、U1330202）

Research on Dynamic Fracture Behavior of Polymer Bonded Explosive Simulant Based on Cohesive Crack Model

CUI Yun-xiao^{1, 2}, CHEN Peng-wan¹, GUO Bao-qiao¹, David A. Cendón³, ZHOU Zhong-bin¹

(1.State Key Laboratory of Explosion Science and Technology，Beijing Institute of Technology, Beijing 100081, China; 2.Northwest Institute of Nuclear Technology, Xi'an 710024, Shaanxi，China; 3.Technical University of Madrid，Madrid 28040, Spain)

Received:2017-01-10 Revised:2017-01-10 Online:2018-02-01

摘要/Abstract

摘要： 对某高聚物粘结炸药（PBX）模拟材料的动态拉伸断裂行为进行研究。针对该材料开展了基于霍普金森压杆的动态带预制裂纹半圆盘弯曲实验，并结合高速摄像与数字图像相关方法，得到了试样动态破坏过程中的位移场和应变场。基于内聚裂纹模型，对其动态拉伸破坏过程进行了数值模拟。数值模拟与实验结果进行对比后发现，拉伸应力曲线、试样破坏前后变形场等结果符合较好。根据数值模拟结果，分析了PBX试样在动态预制裂纹半圆盘弯曲实验过程中的裂纹扩展演化规律，得到裂纹宽度比实验结果偏小约15%的结论。

关键词: 爆炸力学, 内聚裂纹模型, 半圆盘弯曲实验, 高聚物粘结炸药, 数字图像相关方法

Abstract: The dynamic tensile fracture behavior of polymer bonded explosive simulant was investigated. The experimental test was performed on notched semi-circular bending (NSCB) samples of the material by using the split Hopkinson pressure bar(SHPB) apparatus. With the aide of a high-speed camera, the dynamic displacement and strain field during the dynamic fracture process were obtained by the digital image correlation (DIC) technique. Based on cohesive crack model (CCM), the numerical simulation of the same conditions was performed. Compared with the results obtained by simulation and experiment, the good agreement was found for the time history of tensile stress and the displacement and strain fields during dynamic fracture. The behavior of crack propagation of PBX during NSCB test was analyzed by the CCM. Furthermore, the width of crack in NSCB sample is about 15% smaller than the experimental results. Key

Key words: explosionmechanics, cohesivecrackmodel, dynamicNSCBexperiment, polymerbondedexplosive, techniqueofdigitalimagecorrelation

中图分类号:

崔云霄，陈鹏万，郭保桥， David A. Cendón，周忠彬. 基于内聚裂纹模型的高聚物粘结炸药模拟材料动态断裂行为研究[J]. 兵工学报, 2017, 38(12): 2379-2385.

CUI Yun-xiao, CHEN Peng-wan, GUO Bao-qiao, David A. Cendón, ZHOU Zhong-bin. Research on Dynamic Fracture Behavior of Polymer Bonded Explosive Simulant Based on Cohesive Crack Model[J]. Acta Armamentarii, 2017, 38(12): 2379-2385.

参考文献

［1］陈鹏万，黄风雷. 含能材料损伤理论及应用[M]. 北京: 北京理工大学出版社, 2006.
CHEN Peng-wan, HUANG Feng-lei. Damage theory and application of energetic materials[M]. Beijing: Beijing Institute of Technology Press, 2006. (in Chinese)

[2] Grantham S G, Siviour C R, Proud W G, et al. High-strain rate Brazilian testing of an explosive simulant using speckle metrology[J]. Measurement Science and Technology, 2004, 15(9): 1867-1870.
[3] Zhou Y X, Xia K, Li X B, et al. Suggested methods for determining the dynamic strength parameters and mode-I fracture toughness of rock materials[J]. International Journal of Rock Mechanics & Mining Sciences, 2012, 49:105-112.
[4] Zhou Z B, Chen P W, Duan Z B. Comparative study of the fracture toughness determination of a polymer-bonded explosive stimulant [J]. Engineering Fracture Mechanics, 2011,78(17): 2991-2997.
[5] Chen R, Cheng L, Lin Y, et al. Studies on the dynamic fracture properties and failure modes of a PBX[J]. International Journal of Applied Mechanics， 2014, 6(4):1450039.
[6] Dienes J K, Zuo Q H, Kershner J D. Impact initiation of explosives and propellants via statistical crack mechanics[J]. Journal of the Mechanics and Physics of Solids, 2006, 54(6):1237-1275.
[7] 傅华，李俊玲，谭多望. PBX炸药动态Brazilian试验及数值模拟研究[J]. 高压物理学报, 2012, 26(2): 148-154.
FU Hua, LI Jun-ling, TAN Duo-wang. Dynamic Brazilian test and simulation of plastic-bonded explosives [J]. Chinese Journal of High Pressure Physics, 2012, 26(2): 148-154. (in Chinese)
[8] 王鹏飞，黄西成，何颖波. 基于线性Drucker-Prager模型的PBX准静态弹塑性变形分析[J]. 含能材料, 2015, 23(5):464-471.
WANG Peng-fei, HUANG Xi-cheng, HE Ying-bo. Quasi-static elastoplastic deformation analysis of PBX based on linear Drucker-Prager model[J]. Chinese Journal of Energetic Materials, 2015, 23(5):464-471.(in Chinese)
[9] 谢凤英，张丘，刘维，等. 高聚物粘结炸药铣削时的边缘崩块形成机理分析[J]. 兵工学报, 2016, 37(5): 823-828.
XIE Feng-ying, ZHANG Qiu, LIU Wei, et al. Preliminary research on formation mechanisms of edge spalling in PBX milling [J]. Acta Armamentarii, 2016, 37(5): 823-828.(in Chinese)
[10] Planas J, Elices M, Guinea G V, et al. Generalizations and specializations of cohesive crack models [J]. Engineering Fracture Mechanics, 2003, 70(14): 1759-1776.
[11] Reyes E, Gálvez J C, Casati M J, et al. An embedded cohesive crack model for finite element analysis of brickwork masonry fracture [J]. Engineering Fracture Mechanics, 2009, 76(12): 1930-1944.
[12] 崔云霄，陈鹏万，David A. Cendón，等.基于内聚裂纹模型的高聚物粘结炸药模拟材料动态巴西实验的数值模拟[J]. 兵工学报, 2016,37 (9): 1639-1645.
CUI Yun-xiao, CHEN Peng-wan, Cendón D A, et al. Numerical simulation of dynamic Brazilian test of polymer bonded explosive simulant based on cohesive crack model[J]. Acta Armamentarii, 2016, 37 (9): 1639-1645. (in Chinese)

第38卷第12期
2017 年12月兵工学报ACTA
ARMAMENTARIIVol.38No.12Dec.2017

[1]	刘纯，欧卓成，段卓平，黄风雷. 动态加载下高聚物粘结炸药中椭圆孔洞坍塌引起的热点温度及其半经验解析表达[J]. 兵工学报, 2022, 43(1): 57-68.
[2]	刘计划，赵宏立，何昌辉，靳建伟，张邹邹，王琼林，赵宝明. 冲击载荷作用下典型发射药的弹性模量分析方法[J]. 兵工学报, 2021, 42(2): 289-296.
[3]	白志玲，段卓平，黄风雷. 高聚物粘结炸药冲击起爆统计热点反应速率模型[J]. 兵工学报, 2021, 42(11): 2379-2387.
[4]	秦金凤，赵雪，钱华，芮久后. 高致密球形黑索今晶体结构对高聚物粘结炸药安全性能的影响[J]. 兵工学报, 2020, 41(3): 481-487.
[5]	刘坚成，张雷雷，徐坤，皮爱国，史文卿，黄风雷. 反弹道非正侵彻的弹体结构响应实验研究[J]. 兵工学报, 2019, 40(9): 1797-1803.
[6]	魏强，黄西成，陈刚，陈鹏万. 高聚物粘结炸药动态损伤破坏的数值刻画[J]. 兵工学报, 2019, 40(7): 1381-1389.
[7]	李潘，郝志明，刘永平，甄文强. 基于近场动力学非普通状态理论的高聚物粘结炸药损伤破坏模拟研究[J]. 兵工学报, 2018, 39(5): 893-900.
[8]	欧亚鹏，闫石，焦清介，郭学永，孙亚伦. 浇注高聚物粘结炸药的粘结剂体系设计及其应用研究[J]. 兵工学报, 2018, 39(1): 63-70.
[9]	冉春，陈鹏万，李玲，张旺峰. 中高应变率条件下TC18钛合金动态力学行为的实验研究[J]. 兵工学报, 2017, 38(9): 1723-1728.
[10]	陈浩玉，洪仁楷，陈永涛，张世文，任国武，莫俊杰. 用于微层裂物质诊断的小型动量探针技术[J]. 兵工学报, 2017, 38(9): 1729-1735.
[11]	唐廷，周健南. 地震后地下受损拱结构的抗爆炸能力研究[J]. 兵工学报, 2017, 38(9): 1736-1744.
[12]	杨军，李焰，张德志，史国凯，张敏，刘文祥，王昭，熊琛. 光子多普勒测速仪与压杆相结合的冲击波反射压力测试技术[J]. 兵工学报, 2017, 38(7): 1368-1374.
[13]	刘俊，田宙，钟巍，谢淑红. 冲击波作用下单层钢化玻璃抗爆性能的数值模拟研究[J]. 兵工学报, 2017, 38(7): 1402-1408.
[14]	王竟成，罗景润. 不同细观力学方法预测高聚物粘结炸药有效模量的比较[J]. 兵工学报, 2017, 38(6): 1106-1112.
[15]	李勇，程远胜，张攀，刘均. 空中爆炸载荷下梯度波纹夹层板抗爆性能仿真研究[J]. 兵工学报, 2017, 38(6): 1131-1139.

基于内聚裂纹模型的高聚物粘结炸药模拟材料动态断裂行为研究

Research on Dynamic Fracture Behavior of Polymer Bonded Explosive Simulant Based on Cohesive Crack Model

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价