成型工艺对24-二硝基苯甲醚基熔铸炸药装药质量的影响

doi:10.3969/j.issn.1000-1093.2018.09.007

摘要/Abstract

摘要： 为了提高2,4-二硝基苯甲醚（DNAN）基熔铸炸药的装药质量，采用压力浇铸与真空浇铸成型工艺，研究其对DNAN基熔铸炸药温度场、缩孔疏松、相对密度及抗拉强度的影响规律。结果表明：压力浇铸使DNAN基熔铸炸药凝固时间缩短，药柱内部缩孔疏松及气孔减少；当成型压力达到0.8 MPa时，DNAN/奥克托今（HMX）炸药相对密度和抗拉强度分别提高了6.4%、9.9%，药柱无裂纹；DNAN/黑索今（RDX）炸药的相对密度提高了2.7%，但抗拉强度降低了40.8%，同时药柱存在裂纹。真空浇铸对DNAN基熔铸炸药凝固过程温度场无影响，使药柱内部缩孔疏松及气孔减少；当真空度达到0.08 MPa时，DNAN/RDX炸药的相对密度及抗拉强度分别提高了2.0%、14.3%，药柱无裂纹。因此，为了获得高质量的熔铸炸药，DNAN/HMX炸药可采用压力浇铸；DNAN/RDX炸药可采用真空浇铸。

关键词: 2, 4-二硝基苯甲醚, 熔铸炸药, 成型工艺, 温度场, 缩孔疏松, 相对密度, 抗拉强度

Abstract: Pressure casting and vacuum casting are used to improve the charge quality of DNAN-based melt-cast explosives, and the influences of casting precess on the temperature field, shrinkage porosity, relative density and tensile strength of DNAN-based melt-cast explosive are investigated. The results show that pressure casting can shorten the solidification time of DNAN-based melt-cast explosive and reduce its shrinkage cavity and porosity. When the molding pressure reaches 0.8 MPa, the relative density and tensile strength of DNAN/HMX explosives are increased by 6.4% and 9.9%, respectively, and no cracks are found in the grain. As for DNAN/RDX explosives, the relative density can be increased by 2.7%, and the tensile strength can be reduced by 40.8%, but the cracks exist in the grain. Although vacuum casting has no effect on the temperature field in solidification process, it can reduce the shrinkage cavity and porosity. When the vacuum degree reaches 0.08 MPa, the relative density and tensile strength of DNAN/RDX explosives are increased by 2.0% and 14.3%, respectively, and no cracks are found in the grain. Therefore, pressure casting and vacuum casting can be used respectively to improve the charge quality of DNAN/HM explosives and DNAN/RDX explosives.Key

Key words: 2,4-dinitroanisole(DNAN), melt-castexplosive, formingprocess, temperaturefield, shrinkageporosity, relativedensity, tensilestrength

中图分类号:

TQ564.4
TJ55

蒙君煚，周霖，金大勇，牛国涛，王亲会. 成型工艺对24-二硝基苯甲醚基熔铸炸药装药质量的影响[J]. 兵工学报, 2018, 39(9): 1719-1726.

MENG Jun-jiong， ZHOU Lin, JIN Da-yong， NIU Guo-tao, WANG Qin-hui. Effect of Forming Process on Casting Quality of 24-Dinitroanisole-based Casting Explosive[J]. Acta Armamentarii, 2018, 39(9): 1719-1726.

参考文献

［1］ Doll D W, Hanks J M, Allrend A G. Reduced sensitivity, melt-pourable TNT replacements: US, 7067024 ［P］. 2006-06-27.
［2］王永川, 唐兴民. 梯黑药柱的改性研究［J］. 含能材料, 1994, 2(1): 7-11.
WANG Yong-chuan, TANG Xing-min. Study on modification of cast TNT-RDX charges ［J］. Chinese Journal of Energetic Materials, 1994, 2(1):7-11.(in Chinese)
［3］ Nicolich S, Niles J, Ferlazzo P, et al. Recent developments in reduced sensitivity melt-pour explosives ［C］∥Proceedings of the 34th Interactional Annual Conference of ICT. Karisruhe, Germany: Fraunhofer Institute for Chemical Technology, 2003: 24-27.
［4］ Niles J, Doll D. Development of a practical reduced sensitivity composition B replacement ［C］∥Proceedings of the 32th International Annual Conference of ICT. Karlsruhe, Germany: Fraunhofer Institute for Chemical Technology, 2001, 28: 1-8.
［5］ Fedoroff B T. Dictionary of a explosives, ammunition and weapons (German section), Technical Report 2510 ［R］. Dover, NJ, US: Picatinny Arsenal, 1958.
［6］ Doll D W, Hanks J M, Allred A G, et al. Reduced sensitivity melt-pourable tritonal replacements: US, 6964714 ［P］. 2005-11-15.
［7］ Wilson A. Explosive ingredients and compositions for the IM M795 artillery ammunition ［C］∥Insensitive Munitions and Energetic Materials Technology Symposium. Miami, FL, US: National Defense Industrial Association, 2007.
［8］ Davies P J, Provatas A. Characterisation of 2, 4-dinitroanisole: an ingredient for use in low sensitivity melt cast formulations, Report DSTO-TR-1904 ［R］. Canberra, Australian: Defence Science and Technology Organisation, 2006.
［9］邢书明, 荣振升. 加压凝固过程的谐调方程［J］. 中国铸造装备与技术, 1997(1): 46-49.
XING Shu-ming, RONG Zhen-sheng. Pressed solidification process equation of compatibility ［J］. China Foundry Machinery & Technology, 1997(1): 46-49.(in Chinese)

［10］ Hammer Johansen , Digre Kristiansen J, Gjerse R, et al. RDX and HMX with reduced sensitivity towards shock initiation-RS-RDX and RS-HMX ［J］. Propellants, Explosives, Pyrotechnics, 2008, 33(1): 20-24.
［11］花成, 黄明, 黄辉, 等. RDX/HMX 炸药晶体内部缺陷表征与冲击波感度研究［J］. 含能材料, 2010, 18(2): 152-156.
HUA Cheng, HUANG Ming, HUANG Hui, et al. Intra-granular defects and shock sensitivity of RDX/HMX ［J］. Chinese Journal of Energetic Materials, 2010, 18(2): 152-156.(in Chinese)
［12］黄亨建, 董海山, 舒远杰, 等. HMX 中晶体缺陷的获得及其对热感度和热安定性的影响［J］. 含能材料, 2003, 11(3): 123-126.
HUANG Heng-jian, DONG Hai-shan, SHU Yuan-jie, et al. The preparation of HMX crystals with defects and the influences of crystal defects on thermal sensitivity and stability ［J］. Chinese Journal of Energetic Materials, 2003, 11(3): 123-126.(in Chinese)
［13］ Stoltz C A, Mason B P, Hooper J. Neutron scattering study of internal void structure in RDX ［J］. Journal of Applied Physics, 2010, 107(10): 103527-1-103527-6.
［14］李忠友, 邹庆勇, 姚南, 等. 一种火炸药药浆真空震动浇注系统: 中国, CN103204750A ［P］. 2013-07-17.
LI Zhong-you, ZOU Qing-yong, YAO Nan,et al. A kind of vacuum shocking system for explosive slurry: China, CN103204750A ［P］. 2013-07-17.(in Chinese)
［15］ Witt W, Sabranski U. A new method for cast-loading mixtures of explosives ［J］. Propellants, Explosives, Pyrotechnics, 1979, 4(1): 1-3.
［16］张金勇, 胡双启, 曹雄. 两种新型装药工艺［J］. 工业安全与环保, 2006, 32(4): 56-57.
ZHANG Jin-yong, HU Shuang-qi, CAO Xiong. Introductions on two kinds of new type charging process ［J］. Industrial Safety and Environmental Protection, 2006, 32(4): 56-57.(in Chinese)
［17］ Niyama E, Uchida T, Morikawa M, et al. A method of shrinkage prediction and its application to steel casting practice ［J］. Intentional Cast Metals Journal, 1982, 7(3): 52-63.
［18］ Lee P D, Chirazi A, See D. Modeling microporosity in aluminum-silicon alloys: a review ［J］. Journal of Light Metals, 2001, 1(1): 15-30.
［19］ Zhang D L, Cantor B. Numerical heat flow model for squeeze casting Al alloys and Al alloy/SiCp composites ［J］. Modeling and Simulation in Materials Science and Engineering, 1995, 3(1): 121-130.
［20］魏红梅. 挤压铸造SiC_w/Al-18Si复合材料凝固行为的研究［D］. 哈尔滨：哈尔滨工业大学, 2009.
WEI Hong-mei. Solidification of SiC_w/Al-18Si composites prepared by squeeze casting ［D］. Harbin: Harbin Institute of Technology, 2009.(in Chinese)
［21］ Grau H, Gandzelko A, Samuels P. Solubility determination of raw energetic materials in molten 2,4-dinitroanisole ［J］. Propellants, Explosives, Pyrotechnics, 2014, 39(4): 604-608.

第39卷
第9期2018 年9月兵工学报ACTA
ARMAMENTARIIVol.39No.9Sep.2018

[1]	余毅磊, 王晓东, 任文科, 高光发. 三层组合陶瓷复合装甲的抗侵彻性能及其损伤机制[J]. 兵工学报, 2024, 45(1): 44-57.
[2]	李云飞, 高鑫, 陈鹏万, 刘开源. TiB₂/B₄C复相陶瓷自蔓延热爆炸烧结与性能表征[J]. 兵工学报, 2024, 45(1): 26-34.
[3]	陶磊, 刘检华, 夏焕雄, 敖晓辉, 高丰. 基于B样条神经网络的熔铸装药温度场预测[J]. 兵工学报, 2023, 44(5): 1339-1349.
[4]	陈漫, 刘宇键, 于亮, 王旭, 张存振, 胡淋. 湿式多片离合器结构特征对接触压力特性的影响[J]. 兵工学报, 2023, 44(2): 406-416.
[5]	张鑫, 林凡, 沈鑫杰. 基于改进SOGI-FLL的旋转弹舵机滞后测试方法[J]. 兵工学报, 2023, 44(2): 428-436.
[6]	尤浩, 常新龙, 赵久奋, 张有宏, 王顺宏. 带攻击角度约束的三维领弹-从弹时间协同制导律[J]. 兵工学报, 2023, 44(11): 3369-3381.
[7]	金嘉玺, 杨树军, 彭增雄, 陈俏儿, 李学良, 潘辉, 连壮. 基于等效传热和动态热流分配的限滑离合器温度场研究[J]. 兵工学报, 2023, 44(10): 3056-3066.
[8]	杨春伟, 刘炳琪, 王继平, 邵节, 韩治国. 基于注意力机制的高超声速飞行器LSTM智能轨迹预测[J]. 兵工学报, 2022, 43(S2): 78-86.
[9]	李博，王博，韩京冶，杨宗睿，栗霖雲，傅畅之. 基于车载计算机的红外图像移动目标检测[J]. 兵工学报, 2022, 43(S1): 66-73.
[10]	余毅磊, 王晓东, 任文科, 马铭辉, 蒋招绣, 高光发. 陶瓷/金属复合靶受12.7mm穿甲燃烧弹侵彻时弹靶破碎特征[J]. 兵工学报, 2022, 43(9): 2307-2317.
[11]	王晓东, 徐永杰, 董方栋, 王昊, 郑娜娜. 凯夫拉与陶瓷复合结构抗侵彻性能数值仿真[J]. 兵工学报, 2022, 43(9): 2360-2366.
[12]	李淑睿，段卓平，白志玲，张旭，黄风雷. 2，4-二硝基苯甲醚基熔铸含铝炸药冲击起爆特性[J]. 兵工学报, 2022, 43(6): 1288-1294.
[13]	阚润哲，聂建新，郭学永，闫石，焦清介，张韬. 不同铝氧比CL-20基含铝炸药深水爆炸能量输出特性[J]. 兵工学报, 2022, 43(5): 1023-1031.
[14]	刘瑞峰, 王昕捷, 黄风雷, 黄亨建. 2，4-二硝基苯甲醚基熔铸炸药宏细观烤燃响应特性数值分析[J]. 兵工学报, 2022, 43(2): 287-296.
[15]	江胜华. 基于磁偶极子的2阶磁场梯度张量缩并方法[J]. 兵工学报, 2022, 43(12): 3122-3131.