Simulation Investigation on Crack Initiation and Propagation in Ultrasonic Assisted Grinding of Ceramics Material

doi:10.3969/j.issn.1000-1093.2016.05.017

Abstract

Abstract: Based on smoothed particle hydrodynamics (SPH) method, the initiation and propagation of the cracks in the process of single abrasive impacting a workpiece are simulated during ultrasonic assisted grinding of ceramics material, and the removal characteristics and surface layer damage of material under different ultrasonic impact speeds are revealed. The simulation results show that the lateral and radial cracks occur initially when single abrasive is pressed into the workpiece at a certain depth under different impact speeds. With the increase in impact speed, the fractures in action area are significantly reduced, and the critical pressed depth of abrasive is decreased when a lateral crack is generated, while the critical pressed depth of abrasive is unchanged obviously when a radial crack is generated. By observing the propagation of the two kinds of crack with the increase in the pressed depth, it can be found that the propagation velocity and geometric size of lateral crack decrease, while the radial crack has no obvious change. The results show that the ductile region removal of ceramics material is enhanced with the increase in impact speed, while the damage of surface layer is not enlarged, and the surface quality is improved.

Key words: manufacturing technology and equipment, ultrasonic assisted grinding, crack initiation and propagation, smoothed particle hydrodynamics method

CLC Number:

TG580.1

LIANG Zhi-qiang， TIAN Meng， WANG Qiu-yan， WANG Xi-bin，. Simulation Investigation on Crack Initiation and Propagation in Ultrasonic Assisted Grinding of Ceramics Material[J]. Acta Armamentarii, 2016, 37(5): 895-902.

References

［1］ Ishihara M, Baba S, Takahashi T, et al. Fundamental thermo mechanical properties of SiC-based structural ceramics subjected to high energy particle irradiations[J]. Fusion Engineering and Design, 2000, 51: 117-121.
[2］陈维平, 韩孟岩, 杨少锋. Al₂O₃陶瓷复合材料的研究进展[J]. 材料工程, 2011, 21(3): 91-96.
CHEN Wei-ping, HAN Meng-yan, YANG Shao-feng. Research progress of Al₂O₃ ceramic composites[J]. Journal of Materials Engineering, 2011, 21(3): 91-96. (in Chinese)
[3］ Saito T, Kawamoto H, Yamamoto T, et al. Lattice strain and dislocations in polished surfaces on sapphire[J]. Journal of the American Ceramic Society, 2005, 88(8): 2277-2285.
[4］ Liang Z, Wu Y, Wang X, et al. A new two-dimensional ultrasonic assisted grinding (2D-UAG) method and its fundamental performance in monocrystal silicon machining[J]. International Journal of Machine Tools and Manufacture, 2010, 50(8): 728-736.
[5］ Tawakoli T, Azarhoushang B, Mohammad R. Ultrasonic assisted dry grinding of 42CrMo4[J]. The International Journal of Advanced Manufacturing Technology, 2009, 42(9/10): 883-891.
[6］ Uhlmann E, Spur G. Surface formation in creep feed grinding of advanced ceramics with and without ultrasonic assistance[J]. CIRP Annals-Manufacturing Technology, 1998, 47(1): 249-252.
[7］米召阳, 梁志强, 王西彬, 等. 基于光滑粒子流体动力学法单颗磨粒超声辅助磨削陶瓷材料的磨削力仿真研究[J]. 兵工学报, 2015, 36(6): 1067-1073.
MI Zhao-yang, LIANG Zhi-qiang, WANG Xi-bin, et al. A simulation investigation on grinding forces in ultrasonic assisted grinding of ceramics with single abrasive grain by using SPH method[J]. Acta Armamentarii, 2015, 36(6): 1067-1073. (in Chinese)
[8］樊俊铃, 郭杏林. 弹塑性疲劳裂纹扩展行为的数值模拟[J].机械工程学报, 2015, 51(10): 33-40.
FAN Jun-ling, GUO Xing-lin. Numerical simulation on elastic-plastic fatigue crack growth behavior[J]. Journal of Mechanical Engineering, 2015, 51(10): 33-40.(in Chinese)
[9］徐世龙, 林建忠, 杨玉廷. 基于SPH方法的磨削机理仿真研究[J].制造技术与机床, 2012(12): 136-139.
XU Shi-long, LIN Jian-zhong, YANG Yu-ting. Simulation study of grinding mechanism based on SPH[J]. Manufacturing Technology & Machine Tool, 2012(12): 136-139. (in Chinese)
[10］ Lucy L. A numerical approach to the testing of the fission hypothesis[J]. Astronomical Journal, 1977, 82(12): 1013-1024.
[11］ Gingold R, Monaghan J. Smoothed particle hydrodynamics：theory and application to non-spherical stars[J]. Monthly Notices of the Royal Astronomical Society, 1977, 181(3): 375-389.
[12］ Monaghan J. An introduction to SPH[J]. Computer Physics Communications, 1988, 48(1): 89-96.
[13］ Ruttimann N, Buhl S, Wegener K. Simulation of single grain cutting using SPH method[J]. Journal of Machine Engineering, 2010, 10(3): 17-29．
[14］ Wang J, Shimada K, Mizutani M, et al. Material removal during ultrasonic machining using smoothed particle hydrodynamics[J]. International Journal of Automation Technology, 2013, 7(6): 614-620.
[15］龚江宏. 陶瓷材料断裂力学[M]. 北京：清华大学出版社, 2001.
GONG Jiang-hong. Fracture mechanics of ceramics[M]. Beijing:Tsinghua University Press, 2001. (in Chinese)
[16］ Cronin D, Bui K, Kaufmann C, et al. Implementation and validation of the Johnson-Holmquist ceramic material model in LS-Dyna[C]∥4th European LS-DYNA Users Conference. Ulm, Germany: ARUP,2003.
[17］ Liang Z, Wang X, Wu Y, et al. Experimental study on brittle-ductile transition in elliptical ultrasonic assisted grinding (EUAG) of monocrystal sapphire using single diamond abrasive grain[J]. International Journal of Machine Tools and Manufacture, 2013, 71(8): 41-51.

[1]	ZHANG Fa-ping, WU Di, ZHANG Ti-guang, ZHANG Ling-yun, YANG Ji-bin. Independent Component Analysis Based on Machining Error Separation [J]. Acta Armamentarii, 2016, 37(9): 1692-1699.
[2]	QIN Guo-hua, SUN Shuo, WANG Hua-min, ZUO Dun-wen, WU Tie-jun, LU Yu-ming. A Reverse Direction Iterative Planning Algorithm of Clamping Forces in Entire Active Region Based on Workpiece Stability [J]. Acta Armamentarii, 2016, 37(9): 1700-1707.
[3]	GONG Ya-dong, SUN Yao, LIU Yin. Experimental Investigation and Modeling of Three-dimensional Surface Roughness in LS-WEDM of TC4 [J]. Acta Armamentarii, 2016, 37(6): 1058-1065.
[4]	LI Hui-juan, MING Ping-mei, ZHOU Tao, ZHAO Yun-long, QIN Ge. Research on Distribution Uniformity of Electroformed Metal Layer by Using Hollow Square Cathode-shielding Plate [J]. Acta Armamentarii, 2016, 37(6): 1075-1081.
[5]	WANG Jia-bin， LI Shu-juan， LIANG Lie， TANG Ao-fei， MA Lei. Modeling and Experiment of Contact Arc Length in SiC Monocrystal Cutting [J]. Acta Armamentarii, 2016, 37(5): 879-887.
[6]	WANG Feng-biao, HOU Bo， YUAN Kai, WU Di, ZHOU Lian-jie. Research on Milling of Ni-based Alloy Honeycomb Material at Ice Fixation and Cryogenic Temperatures [J]. Acta Armamentarii, 2016, 37(5): 888-894.
[7]	WANG Xin-gang， LYU Chun-mei， ZHAO Yu-qian， CHEN Xiao-ming. Research on Failure-rate-based Tool Replacing Strategy [J]. Acta Armamentarii, 2016, 37(5): 903-908.
[8]	HU De-jin. Precision Generated Grinding Method and Its Technology of Large Diameter SiC Aspheric Surface [J]. Acta Armamentarii, 2016, 37(12): 2340-2346.
[9]	HU De-jin. Research on Intelligent Precision Grinding Method and Control Model of Annular Inner and Outer sphere [J]. Acta Armamentarii, 2015, 36(9): 1743-1749.
[10]	PAN Qin-xue， LIU Shuai， XIAO Ding-guo， JIN Xin. The Method of Gear Residual Stress Measurement Based on Ultrasonic Technology [J]. Acta Armamentarii, 2015, 36(9): 1757-1765.
[11]	MA Qun, LI Yan, YANG Ming-shun, YUAN Qi-long, LI Yu-xi. Structure Improvement of Roll-beating Head for Continuous Indexing Cold Roll-beating Machine [J]. Acta Armamentarii, 2015, 36(8): 1587-1593.
[12]	LI Yu-xi, LI Yan, YANG Ming-shun, CUI Feng-kui, HE Xuan-jing. Investigation of the Tooth Profile Error Based on the Forming Theory of Balloscrew Manufactured by Cold Rolling [J]. Acta Armamentarii, 2015, 36(8): 1594-1600.
[13]	WANG Feng-biao, ZHANG Jin-bao, MA Yu-yong, HOU Bo, WANG Yong-qing. Research on Milling Process of Aramid Fiber Reinforced Composite Materials in Cryogenic Conditions [J]. Acta Armamentarii, 2015, 36(11): 2141-2148.
[14]	GUO Cheng-bo, DI Shi-chun, WEI Dong-bo, SONG Yun-long, WU Xiang. Research on Efficient Electrical Discharge Milling of TC4 Titanium Alloy [J]. Acta Armamentarii, 2015, 36(11): 2149-2156.
[15]	JIANG Zhen-xi, SUN Jie, LI Guo-chao, JIA Xing-min, LI Jian-feng. Investigation on the Relationship among Tool WearCutting Force and Vibration in Milling of TC4 [J]. Acta Armamentarii, 2015, 36(1): 144-150.