Effect of Thermo-mechanical Treatment on the Microstructure and Mechanical Properties of a Medium Carbon Cr-Ni-W-Mo Steel

doi:10.3969/j.issn.1000-1093.2020.09.023

Abstract

Abstract: In order to further improve the strength and ductility of the medium carbon Cr-Ni-W-Mo steel， the effect of thermo-mechanical treatment (TMT)，which was conducted at 700 ℃ with deformation from 20% to 50%，on the microstructure evolution and mechanical properties of medium carbon Cr-Ni-W-Mo steel was analyzed by scanning electron microscopy (SEM)，transmission electron microscopy(TEM)，electron backscattered diffraction (EBSD) and tensile test. The results show that the microstructures of steel after TMT processing contain the complex phases with tempered martensite，lower bainite and retained austenite.The fractions of lower bainite and retained austenite，and the dislocation density increase together with the refinement of martensite lath with the deformation increasing from 20% to 50%. Due to the coupling effects of phase transformation strengthening，fine grain strengthening and dislocation strengthening，the strength and ductility of steel are improved simultaneously with the increase in deformation. The steel processed by TMT with deformation of 50% has high strength and good ductility，and its yield strength，ultimate strength and elongation are 1 733 MPa， 2 243 MPa and 12.66%，respectively， which are improved by 28.18%，12.88% and 50.35% than those of the steel processed by conventional heat treatment，respectively.

Key words: mediumcarbonCr-Ni-W-Mosteel, thermo-mechanicaltreatment, lowerbainite, mechanicalproperty

CLC Number:

TG142.12

LIANG Jiaxin， WANG Yingchun， CHENG Xingwang， LI Zhuang， LI Shukui. Effect of Thermo-mechanical Treatment on the Microstructure and Mechanical Properties of a Medium Carbon Cr-Ni-W-Mo Steel[J]. Acta Armamentarii, 2020, 41(9): 1904-1912.

References

［1］张国星，强洪夫，陈福振，等. 钻地弹侵彻地下工事问题的研究与发展[J].飞航导弹，2018(6): 34-38.
ZHANG G X，QIANG H F，CHEN F Z，et al. Research and development of ground-penetrating bombs penetrating underground work[J]. Aerodynamic Missile Journal，2018(6): 34-38. (in Chinese)
[2] 程皓.地下毁伤性目标定位的研究与实现[D].太原:中北大学，2019.
CHENG H.Research and implementation of underground damage target positioning [D]. Taiyuan: North University of China，2019. (in Chinese)
[3] 成丽蓉，汪德武，贺元吉.侵彻单层和多层靶时战斗部装药损伤及热点生成机理研究[J].兵工学报，2020，41(1):32-39.
CHENG L R，WANG D W，HE Y J. Research on the damage and hot-spot generation in explosive charges during penetration into single or multi-layer target[J].Acta Armamentarii，2020，41(1):32- 39. (in Chinese)
[4] 党爱国，李晓军.国外钻地武器发展回顾及展望[J]. 飞航导弹，2014(6): 35-39.
DANG A G，LI X J. Retrospect and prospect of the development of drilling weapons abroad[J]. Aerodynamic Missile Journal，2014(6): 35-39. (in Chinese)
[5] 马田，李鹏飞，周涛，等. 地弹动能侵彻战斗部技术研究综述[J].飞航导弹，2018(4): 83-86.
MA T，LI P F，ZHOU T，et al. A summary of research on the technology of penetration warhead of ground-penetrating bomb[J].Aerodynamic Missile Journal，2018(4): 83-86. (in Chinese)
[6] HERNG-JENG J.Lower-cost，ultra-high-strength， high-toughness steel: US9051635 [P]. 2016-12-29.
[7] KUEHMANN C J，OLSON G B，HERNGJENG J. Nanocarbide precipitation strengthened ultrahigh-strength，corrosion resistant，structural steels: EP20100151760 [P]. 2010-07-14.
[8] KANNAN R，WANG Y Y，NOURI M，et al. Instrumented indentation study of bainite/martensite duplex microstructure[J]. Materials Science and Engineering:A，2018，713: 1-6.
[9] 孙正，赵飞，黄芳.形变量对形变热处理中国低活化马氏体钢显微组织的影响[J].材料热处理学报，2018，39(7): 80-85.
SUN Z，ZHAO F，HUANG F. Influence of deformation on microstructure of thermomechanical treated China low activation martensitic steel [J]. Transactions of Materials and Heat Treatment， 2018， 39(7): 80-85. (in Chinese)
[10] 赵凡，刘祖铭，吕学谦，等.粉末冶金Cu-Cr-Zr合金的形变热处理组织及性能[J]. 粉末冶金材料科学与工程，2019，24(4): 385-390.
ZHAO F，LIU Z M，L X Q，et al. Microstructure and properties of powder metallurgical Cu-Cr-Zr alloy by heat-treatment and deformation[J]. Materials Science and Engineering of Powder Metallurgy， 2019，24(4): 385-390. (in Chinese)
[11] 王琳，马华，陈晨，等. 高锰铸钢的高温形变热处理及其组织和力学性能[J].上海金属，2019，41(4): 40-44.
WANG L，MA H，CHEN C，et al. High-temperature thermo-mechanical treatment and resulting microstructures and mechanical properties for high-manganese cast steel [J]. Shanghai Metals，2019， 41(4): 40-44. (in Chinese)
[12] LI S，ZHU R，KARAMAN I，et al. Development of a kinetic model for bainitic isothermal transformation in transformation-induced plasticity steels[J].Acta Materials，2013，61(8): 2884- 2894.
[13] GHOSH A，GHOSH M. Tensile and impact behavior of thermo-mechanically treated and micro-alloyed medium carbon steel bar[J].Construction and Building Materials，2018，192(4): 657-670.
[14] BASIRUDDIN M，KHAN A K，LENKA S，et al. Effect of microstructure and texture on the impact transition behaviour of thermo-mechanically treated reinforcement steel bars [J]. Materials & Design， 2016， 90: 1136-1150.
[15] WANG B，LIU Z Y，ZHOU X G，et al. Precipitation behavior of nanoscale cementite in 0.17% carbon steel during ultra fast cooling (UFC) and thermomechanical treatment(TMT)[J].Materials Science and Engineering: A，2013，588: 167-174.
[16] XIONG Z P，KOSTRYZHEV A G，CHEN L，et al. Microstructure and mechanical properties of strip cast TRIP steel subjected to thermo-mechanical simulation [J]. Materials Science and Engineering: A， 2016，677: 356-366.
[17] XU X X，BAI B Z，LIU D Y，et al. Effect of thermos-mechanical treatment temperature on structure and properties of CFB/M ultra-high strength steel[J]. Journal of Iron and Steel Research，2010，17(4): 66-72.
[18] 王敏.奥氏体变形对一种Fe-C-Mn-Si先进贝氏体钢相变动力学和组织的影响[D].武汉：武汉科技大学， 2016.
WANG M. The effect of austenite deformation on kinetics and microstructure of bainitic transformation of a Fe-C-Mn-Si advanced bainitic steel[D].Wuhan: Wuhan University of Science and Technology， 2016.(in Chinese)
[19] 潘大刚，杜林秀，王国栋.形变热处理工艺对马氏体和贝氏体金相组织的影响[J].钢铁研究，2004,32(3):25-29.
PAN D G，DU L X，WANG G D. Effect of ausforming process on the morphology of martensite and bainite[J].Research on Iron & Steel，2004，32(3):25-29. (in Chinese)
[20] 王晓南.热轧超高强汽车板析出行为研究及组织性能控制[D].沈阳：东北大学，2011.
WANG X N. Precipitation behavior study and control on microstructure and properties of hot-rolled ultra-high strength automobile strip[D].Shenyang: Northeastern University，2011. (in Chinese)
[21] MANDAL S，TEWARY N K，GHOSH S K，et al. Thermo-mechanically controlled processed ultrahigh strength steel: microstructure， texture and mechanical properties[J].Materials Science and Engineering:A， 2016，663:126-140.
[22] 顾艳，常红英. 27SiMnMoVB钢中粒状贝氏体形成及其回火转变的研究[J].金属材料研究，2009， 35(2):6-13.
GU Y，CHANG H Y. Study on the formation and temper transformation of granular bainite structure in 27SiMnMoVB [J]. Research on Metallic Materials， 2009， 35(2):6-13. (in Chinese)
[23] 陈晓男，刘志鹏，冯艳斌，等.低温回火态新型贝氏体钢的组织性能[J].热加工工艺，2009，38(24):122-125.
CHEN X N，LIU Z P，FENG Y B，et al. Microstructure and pro- perties of new type bainitic steels at low temperature tempering [J]. Hot Working Technology，2009，38(24):122-125. (in Chinese)
[24] 李永亮.700 MPa级高强度汽车大梁钢成分设计与组织控制研究[D].北京: 北京科技大学，2016:139.
LI Y L.Study on composition design and microstructure control about 700 MPa grade high strength beam steel for vehicles[D].Beijing: University of Science and Technology Beijing，2016: 139. (in Chinese)
[25] HAN B，XU Z. Martensitic transformation behavior of large strain deformed Fe-32% Ni alloy [J]. Materials Science and Engineering: A, 2006，431: 109-112.
[26] 王顺兴.金属热处理原理与工艺[M].哈尔滨:哈尔滨工业大学出版社，2009.
WANG S X.Metal heat treatment theory and process [M]. Harbin: Harbin Institute of Technology Press， 2009. (in Chinese)
[27] RYU J H，KIM D I，KIM H S，et al. Strain partitioning and mechanical stability of retained austenite [J]. Scripta Materialia，2010，63(3):297-299.
[28] LI J，TAN Z L，ZHANG M. On the significant impact of deformation coupled with cooling rate during thermo-mechanical controlled processing (TMCP) on microstructure-property relationship in 25Mn2Si2Cr high strength steel[J].Steel Research International， 2019，90(8):1900134.
[29] 袁书强，沈正祥，周春华，等.不同热处理条件下30CrMnSiNi2A钢的组织性能研究[J].材料科学与工程，2015，23(2): 125-128.
YUAN S Q，SHEN Z X，ZHOU C H，et al. Microstructure and property of 30CrMnSiNi2A in different heat treatment[J].Materials Science & Technology，2015，23(2): 125-128. (in Chinese)
[30] 杨璐. DT300高强度钢粉末冶金法制备工艺研究[D]. 洛阳:河南科技大学，2017:55.
YANG L. Research on the preparation of DT300 high-strength steel by powder metallurgy [D]. Luoyang:Henan University of Science and Technology，2017:55. (in Chinese)
[31] 张永皞，李敬民，李昌安.热处理对G50超高强度钢力学性能的影响[J].金属热处理，2019，44(1):54-56.
ZHANG Y H，LI J M，LI C A. Effect of heat treatment on mechanical properties of G50 ultra-high strength steel[J].Heat Treatment of Metals，2019，44(1):54-56. (in Chinese)
[32] 许德明.冷轧退火工艺对奥氏体不锈钢组织和力学性能的作用机理研究[D]. 武汉:武汉科技大学，2019.
XU D M.Study on function mechanism of cold rolling and annealing process on microstructure and mechanical properties of austenitic stainless steel [D].Wuhan: Wuhan University of Science and Technology，2019. (in Chinese)

[1]	KONG Guoqiang, WANG Kang, YU Qiubing, LI Ying, WEI Huazhen, SHAO Meng, BI Weidong, LIU Benxue, YIN Lei, SUN Xiaodong. Properties of Aerogel Modified Quartz Fiber Reinforced Silicone Wave-transparent Composites [J]. Acta Armamentarii, 2022, 43(2): 442-450.
[2]	NIE Zhengyuan， XIAO Jianguang， WANG Yanxin， XIE Zhiyuan. Mechanical Properties and Ignitionand Reaction Characteristics of THV-based Reactive Materials [J]. Acta Armamentarii, 2022, 43(12): 3030-3039.
[3]	JIA Rufeng, YIN Baolin, ZHANG Gaohong, PANG Xinchang, LIU Minying, YANG Guofang, LI Hao, L Qianli. Processing and Characteristics of Polytetrafluoroethylene Based Electromagnetic Shielding Composite Films [J]. Acta Armamentarii, 2022, 43(11): 2916-2923.
[4]	XIONG Manman, YAN Wenmin, XU Cheng, QIN Bin, MA Xuejiao. Ballistic Damage Characteristics of Cowhide as Skin Surrogate [J]. Acta Armamentarii, 2022, 43(1): 29-36.
[5]	LIU Qiang, CHEN Pengwan, SU Jianjun, LI Zhirong, ZHANG Yulei. Tensile Mechanical Properties and Constitutive Model of SiC/polyurea Nanocomposites [J]. Acta Armamentarii, 2021, 42(6): 1238-1249.
[6]	LI Dongwei， MIAO Feichao， ZHANG Xiangrong， XIONG Guosong， ZHOU Lin， ZHAO Shuangshuang. Dynamic Mechanical Properties of an Insensitive DNAN-based Melt-cast Explosive [J]. Acta Armamentarii, 2021, 42(11): 2344-2349.
[7]	HUANG Junhao, WANG Lin, LIU Xiaopin, XU Xuefeng, LIU Anjin, Tayyeb Ali, ZHOU Zhe, NING Zixuan, YANG Jiabin, ZHANG Binbin, CHENG Xingwang. Mechanical Properties and Ballistic Performance of Ti-6321 Alloy [J]. Acta Armamentarii, 2021, 42(1): 124-132.
[8]	XU Baochi， SHI Bikun， FAN Lixia， YANG Chen， FU Yunfeng, DONG Xuehua. Research on Deformation Inhomogeneity along Wall Thickness Direction of Cold Radial Forged Barrel [J]. Acta Armamentarii, 2020, 41(1): 13-20.
[9]	GUO Ruiqi， REN Huiqi， ZHANG Lei， LONG Zhilin， WU Xiangyun， XU Xiangyun， LI Zebin， HUANG Kui. Research Progress of Large-diameter Split Hopkinson Bar Experimental Technique [J]. Acta Armamentarii, 2019, 40(7): 1518-1536.
[10]	GAO Yubo， QIN Guohua, ZHANG Wei， YI Chenhong, DENG Yongjun. Research on Dynamic Compression Properties of TiB₂-B₄C Composite [J]. Acta Armamentarii, 2019, 40(11): 2304-2310.
[11]	HANG Guiyun, YU Wenli, WANG Tao, WANG Jintao, MIAO Shuang. Molecular Dynamics Investigation on Crystal Defect of HMX/NTO Cocrystal Explosive [J]. Acta Armamentarii, 2019, 40(1): 49-57.
[12]	ZENG Xi， PAN Ye， ZHANG Li， JI Shi-ming， CHEN Guo-da， HANG Wei. Analysis of Double-layer Eastic Mechanics and Machining Characteristics of Pneumatic Grinding Wheel [J]. Acta Armamentarii, 2018, 39(9): 1811-1819.
[13]	LI Jun-bao, LI Wei-bing, CHENG Wei, WANG Xiao-ming, LI Wen-bin, HONG Xiao-wen. Mechanical Properties and Constitutive Model of Aluminum Powder/Rubber Composites [J]. Acta Armamentarii, 2018, 39(6): 1186-1194.
[14]	ZHANG Xue-hui， XIE Chen-zhen, LI Xiao-xian， LIU Wei-jiang， YANG Kai， JIANG Miao， ZHU Sheng-jian. Research on Annealing Behaviors of Al₂O₃-Dispersion Strengthened Copper [J]. Acta Armamentarii, 2017, 38(11): 2220-2225.