摘要： 以环戊酮为溶剂，采用冷却结晶的方式制备出毫米级球形黑索今（RDX）晶体，并对溶液浓度、晶种的添加、结晶温度、降温速率、搅拌速率等工艺参数进行分析，对晶体密度、长短轴比、堆积密度以及机械感度进行了测试。结果表明：所获得的毫米级球形RDX晶体表面光滑、结构密实，晶体密度达到1.813 g/cm³，长短轴比≤1.21，堆积密度1.29 g/cm³；机械感度相比于普通RDX显著降低，摩擦感度从82%降低至62%，撞击感度从80%降低至52%.

关键词: 兵器科学与技术, 黒索今, 球形, 冷却结晶, 毫米级

Abstract: The millimeter-scales pheroidized RDX is prepared by cooling crystallization using cyclopentanone as a solvent. The effects of process parameters, such as solution concentration, addition of seed, crystallization temperature, cooling rate, and stirring rate, are investigated. The crystal density, axial ratio, bulk density, and mechanical sensitivity are tested. The results show that the millimeter-grade spheroidized RDX has smooth crystal surface and compact structure. The crystal density is 1.813 g/cm³, the axial ratio is less than 1.21, and the bulk density is 1.26 g/cm³. Its mechanical sensitivity is obviously lower than that of ordinary RDX, the friction sensitivity is decreased from 82% to 62%, and the impact sensitivity is decreased from 80% to 52%.

Key words: ordnance science and technology, RDX, sphere, cooling crystallization, millimeter scale

中图分类号:

TQ564.3

张茂林，贾宏选，毋文莉，刘波，陆明. 冷却结晶制备毫米级球形黑索今[J]. 兵工学报, 2015, 36(11): 2093-2098.

ZHANG Mao-lin, JIA Hong-xuan, WU Wen-li, LIU Bo, LU Ming. Cooling Crystallization Method for Preparation of Millimeter-scale Spheroidized RDX[J]. Acta Armamentarii, 2015, 36(11): 2093-2098.

参考文献

［1］徐瑞娟，陈娅，王东磊.高品质硝基胍的制备与性能表征[C]∥含能材料与钝感弹药技术学术研讨会.成都: 中国工程物理研究院化工材料研究所,2010:260-261.
XU Rui-juan，CHEN Ya，WANG Dong-lei.The preparation and properties of nitroguaridine with high quality[C]∥Academic Seminar on the Technology of Energetic Materials and Insensitive Ammunition.Chengdu: Institute of Chemical Materials,China Academy of Engineering Physics,2010:260-261. (in Chinese)
[2] Watt D，Peugetot F．Reduced sensitivity RDX，where are we[C]∥The 35th International Annual Conference of ICT,Energetic Materials(Structure and Properties).Karlsruhe,Germany：ICT ， 2004．
［E2] Bui-Dang R，Brady V．Evaluation of reduced sensitivity RDX in PBXN一109 in GP bomb[C]∥The 35th International Annual Conference of ICT．Karlsruhe,Germany：ICT ，2004．
[3] Borne L，Beaucamp A．Effects of explosive crystal internal defects on projectile impact initiation[C]∥ The 11th International Detonation Symposium．Snowmass：Office of Naval Research，1998．
[4] Vander S A C. Influence of RDX crystals shape on the shock sensitivity of PBXs[C]∥The 9th Symposium International on Detonation．Portland，Oregon，US：Office of Naval Research，1989．
[5] 叶毓鹏．炸药结晶工艺学及其应用[M]．北京：兵器工业出版社，1995: 20-22.
YE Yu-peng.Technology of explosive crystalization and its application[M].Beijing：Publishing House of Ordnance Industry，1995:20-22.(in Chinese)
[6] 李洪珍，康彬，李金山,等.RDX晶体特性对冲击感度的影响规律［J］. 含能材料,2010，18(5)：487-491.
LI Hong-zhen，KANG Bin，LI Jin-shan，et al. Effects of RDX crystal characteristics on shock sensitivities[J].Chinese Journal of Energetic Materials，2010，18(5)：487-491.(in Chinese)
[7] 荆昌伦，徐复铭，贾宏选，等.粒径150～180 μｍ球形RDX生产工艺研究[J].含能材料,2009,17(2)：194-195.
JING Chang-lun，XU Fu-ming，JIA Hong-xuan，et al.Manufacturing process for the spherical RDX with particle size from 150μm to 180μm[J].Chinese Journal of Energetic Materials，2009,17(2)：194-195.(in Chinese)
[8] 侯会生，毋文莉．浓硝酸重结晶法生产８个类别黑索今工艺研究总结［Ｍ］．山西：国营第575厂，2002：10-12．
HOU Hui-sheng，WU Wen-li.Summary of manufacturing process for eight categories RDX with concertratednitric acidrecrystallization[M].Shanxi：State-run 575 Factory，2002：10-12．(in Chinese)
[9] 任白玉，王鹏，李清霞，等．离子液体-DMSO混合溶剂精制RDX的研究［J］.含能材料,2010，18(6)：639-642.
REN Bai-yu，WANG Peng，LI Qing-xia，et al.Recrystallization of RDX in a iomic liquid-DMSO co-solvent system[J].Chinese Journal of Energetic Materials，2010，18(6)：639-642.(in Chinese)
[10] 荆昌伦，徐复铭，陆明，等.硝酸重结晶法制备导爆管用黑索今［J］. 兵工学报，2010,31（1）：94-98.
JING Chang-lun，XU Fu-ming，LU Ming，et al.Study on lead-RDX prepowed by nitric acid recrystallization[J].Acta Armamentarii，2010,31（1）：94-98.(in Chinese)
[11] 黄明，马军，闫冠云，等.含水环己酮中RDX的结晶介稳特性［J］.含能材料,2012，22(6)：669-673.
HUANG Ming，MA Jun，YAN Guan-yun，et al.Crystallization meta-stable characteristics of RDX in water-containing cycloheranone[J]. Chinese Journal of Energetic Materials，2012，22(6)：669- 673.(in Chinese)
[12] 李明，黄明，徐瑞娟，等.RDX晶体颗粒聚集体压缩刚度曲线的震荡分析［J］.含能材料,2010，18(5)：483-486.
LI Ming，HUANG Ming，XU Rui-juan，et al.Fluctuation analysis of compression curves of RDX crystalline ensembles[J]. Chinese Journal of Energetic Materials，2010，18(5)：483-486.(in Chinese)
[13] 黄明，李洪珍，徐容，等.高品质RDX晶体特性及冲击波起爆特性［J］.含能材料,2011，19(6)：621-623.
HUANG Ming，LI Hong-zhen，XU Rong，et al.Evaluation of crystal properties and initiation characteristics of decreased sensitivity RDX[J]. Chinese Journal of Energetic Materials，2011，19(6)：621-623.(in Chinese)

[1]	薛浩, 王涛, 黄广炎, 崔欣雨, 韩洪伟. 增材制造316L不锈钢球形破片的弹道性能[J]. 兵工学报, 2024, 45(2): 395-406.
[2]	周伯俊, 于传强，刘志浩，柯冰. 基于高压储能的特种车辆快速起竖技术与验证[J]. 兵工学报, 2022, 43(7): 1488-1497.
[3]	高月光，冯顺山，刘云辉，黄岐. 不同端盖厚度的圆柱形装药壳体破片初速分布[J]. 兵工学报, 2022, 43(7): 1527-1536.
[4]	辛大钧，薛琨. 基于人工神经网络的非球形破片阻力系数预测模型[J]. 兵工学报, 2022, 43(5): 1083-1092.
[5]	刘铁磊，徐豫新，王晓锋，张鹏，张健. 钨合金球形破片侵彻低碳钢的弹道极限速度计算模型[J]. 兵工学报, 2022, 43(4): 768-779.
[6]	秦金凤，赵雪，钱华，芮久后. 高致密球形黑索今晶体结构对高聚物粘结炸药安全性能的影响[J]. 兵工学报, 2020, 41(3): 481-487.
[7]	李科斌，李晓杰，王小红，闫鸿浩. 球形装药水下爆炸近场测量的连续探针法研究[J]. 兵工学报, 2019, 40(1): 1-7.
[8]	牟科赛，古勇军，蔺向阳，郑文芳，潘仁明. 水溶性氧化剂在微孔球形药中原位超细化分散方法研究[J]. 兵工学报, 2018, 39(10): 1958-1964.
[9]	娄伟鹏，郑长松，李和言，陈建文，张周立，马源. 高速《Symbol》v湿式换挡离合器排油阀临界开启和关闭压力研究[J]. 兵工学报, 2017, 38(9): 1665-1672.
[10]	王宪成，杨绍卿，马宁，赵文柱. 车辆柴油机缸套动载荷磨损计算模型研究[J]. 兵工学报, 2017, 38(9): 1673-1680.
[11]	孙皓泽，常天庆，王全东，孔德鹏，戴文君. 一种基于分层多尺度卷积特征提取的坦克装甲目标图像检测方法[J]. 兵工学报, 2017, 38(9): 1681-1691.
[12]	张玉燕，孙莎莎，王振春，曹海要，战再吉. 高速载流电枢表面瞬态温度场仿真与测量[J]. 兵工学报, 2017, 38(9): 1692-1698.
[13]	李臣明，宦超，石怀龙. 某箱式火箭炮对面目标分布式杀伤最优火力分配[J]. 兵工学报, 2017, 38(9): 1699-1704.
[14]	雷娟棉，张嘉炜，谭朝明. 小攻角下船尾外形对旋转弹丸马格努斯效应影响的数值研究[J]. 兵工学报, 2017, 38(9): 1705-1715.
[15]	李泽，闫晓鹏，栗苹，郝新红，王建涛. 扫频式干扰对调频多普勒引信的干扰机理研究[J]. 兵工学报, 2017, 38(9): 1716-1722.