热轧后中间退火对5059铝合金耐蚀性能的影响

doi:10.3969/j.issn.1000-1093.2021.02.015

摘要/Abstract

摘要： 为了研究中间退火对舰船用5059铝合金耐蚀性的影响，通过400 ℃/2 h中间退火和57%变形量的冷轧获得了不同5059铝合金板材，分别为热轧板、热轧退火板、直接冷轧板和退火冷轧板。分析了4种不同板材微观组织，并按照美国ASTM G67-2013标准分析了不同板材的耐蚀性。结果表明：400 ℃/2 h退火后，热轧板材内发生部分再结晶，耐蚀性提高，单位面积质量损失由热轧后的8.9 mg/cm²降至3.1 mg/cm²，L-S面的最大腐蚀深度由热轧试样的70 μm降至6 μm；热轧和400 ℃/2 h退火试样经57%变形量的冷轧变形后耐蚀性存在明显差异，单位面积质量损失分别为9.5 mg/cm²和17.3 mg/cm²，L-S面的最大腐蚀深度分别为45 μm和65 μm；热轧板经过400 ℃/2 h退火后L-T面和T-S面由热轧后的剥落腐蚀形貌转变为点蚀形貌，L-S面则由热轧后的沟壑状腐蚀形貌转变为点蚀形貌。

关键词: 5059铝合金, 轧制, 退火, 耐蚀性能, 晶间腐蚀

Abstract: The 5059 aluminum alloy plates, such as hot-rolled plate, hot-rolled annealed plate, direct cold-rolled plate and cold-rolled annealed plate, were prepared with intermediate annealing and cold rolling to study the effect of intermediate annealing on the corrosion resistance of the alloy. The intergranular corrosion properties of different plates were analyzed according to U.S. ASTM G67-2013 standard. The results show that the partial recrystallization happens and the corrosion resistance of the plate is significantly improved after the annealing treatment of hot-rolled plate at 400 ℃ for 2 h. With annealing at 400 ℃ for 2 h, the corrosion weight loss of the hot-rolled plate decreases from 8.9 mg/cm² to 3.1 mg/cm², and the depth of corrosion channel on L-S cross-section decreases from 70 μm to 6 μm. The cold-rolled plates prepared with different states of the hot-rolled plates (with and without annealing) show quite different level of corrosion resistance. The corrosion weight losses of the cold-rolled plates with and without intermediate annealing are 17.3 mg/cm² and 9.5 mg/cm², and the depths of corrosion channel on L-S cross-section of the corresponding plates are 65 μm and 45 μm, respectively. The L-T and T-S cross-sections of hot-rolled plate present exfoliation corrosion morphology, and the L-T cross-section shows gully corrosion morphology. After annealing 400 ℃ for 2 h, the corrosion morphologies of 3 cross-sections are all transformed into pitting morphology.

Key words: 5059aluminumalloy, rolling, annealing, corrosionresistance, intergranularcorrosion

中图分类号:

TG166.3

林洪才，朱庆丰，石入文，贾涛, 张恩阁，赵志浩. 热轧后中间退火对5059铝合金耐蚀性能的影响[J]. 兵工学报, 2021, 42(2): 379-387.

LIN Hongcai, ZHU Qingfeng, SHI Ruwen, JIA Tao, ZHANG Enge, ZHAO Zhihao. Effect of Intermediate Annealing on the Corrosion Resistance of Hot-rolled 5059 Aluminum Alloy[J]. Acta Armamentarii, 2021, 42(2): 379-387.

参考文献

［1］王珏.铝合金在造船中的应用与发展（船用铝合金介绍系列文章之一）[J].轻金属,1994(4):49-54.
WANG J. Application and development of aluminum alloy in shipbuilding (One of a series of articles on marine aluminum alloy) [J]. Light Metals, 1994(4):49-54. (in Chinese)
[2] 王珏.船舶用铝合金材料：船用铝合金介绍系列文章之二[J].轻金属,1994(6):58-64.
WANG J. Aluminum alloy materials for ships (a series of articles on marine aluminum alloy: 2) [J]. Light Metals, 1994(6):58-64. (in Chinese)
[3] 李念奎.船用铝合金的腐蚀性能（1）:船用铝合金介绍系列文章之五[J].轻金属,1994(10):41-47.
LI N K. Corrosion properties of marine aluminum alloy (1) (a series of articles on marine aluminum alloy: 5)[J].Light Metals,1994(10):41-47. (in Chinese)
[4] 李僜谚.5383-H321铝合金板材的形变热处理工艺研究[J].铝加工,2016(3):52-57.
LI D Y, Research on thermo-mechanical treatment process for 5383-H321 aluminum alloy plate[J].Aluminum Fabrication,2016(3): 52-57. (in Chinese)
[5] 占戈,罗兵辉,林汉卿,等.退火温度对冷轧5383铝合金组织及腐蚀性能的影响[J].铝加工,2012(6):16-20.
ZHAN G, LUO B H, LIN H Q, et al. Effect of annealing temperature on microstructure and corrosion properties of cold rolled 5383 aluminum alloy[J]. Aluminum Fabrication,2012(6):16-20.(in Chinese)
[6] ZEHNDER J, PRITZLAFF R, LUNDBERG S, et al. European Aluminum Association aluminum in commercial vehicles[M]. Brussels, Belgium: European Aluminum Association, 2011: 44-49.
[7] KAIGORODOVA L. I. The effect of grain-boundary structure formation on β-precipitation in aged Al-Mg alloys[J]. Materials Science Forum, 1999, 294/295/296:477-480.
[8] SOHI M, SINGH N, SINCLAIR C W, et al. Aging behavior of flexcast Al-Mg alloys with Sc and Zr additions[C]∥Proceedings of the 13rd International Conference on Aluminum Alloys. Pittsburgh, PA, US: Springer, 2012：213-218.
[9] MILJANA P, TAMARA R, ROMHANJI E. Precipitation of the β-phase and corrosion behavior of an Al-6.8 wt.% Mg alloy[C]∥Proceedings of the 13rd International Conference on Aluminum Alloys. Pittsburgh, PA, US: Springer, 2012:363-369.
[10] SCOTTO D, GAIES J, GOLUMBFSKIE W, et al. Direct measurement of the effect of cold rolling on β phase precipitation kinetics in 5xxx series aluminum alloys[J]. Acta Materialia, 2017, 123:264-271.
[11] ROBERT J M, BRIAN Y L, SCOTT W C, et al. The influence of sensitization and corrosion on creep of 5083-H116[J]. Corrosion Science,2018,143:1-9.
[12] PANKAJ K, AKHILENDRA S. Investigation of fatigue and fracture behaviour of sensitized marine grade aluminium alloy AA 5754 [J]. Fatigue & Fracture of Engineering Materials & Structures,2019,42(12):2625-2643.
[13] 王国军. 5383-H321铝合金板材稳定化热处理制度的确定[C]∥ 中国有色金属学会第十二届材料科学与合金加工学术年会论文集.重庆：中国有色金属学会，2007:129-135.
WANG G J. Determination of stabilization heat treatment system for 5383-H321 aluminum alloy plate[C]∥ Proceedings of the 12nd Annual Conference of Materials Science and Alloy Processing of China Nonferrous Metals Society. Chongqing: China Nonferrous Metals Society ,2007:129-135. (in Chinese)
[14] 王月,刘国元.船用5A01铝合金厚板的耐腐蚀性能[J].腐蚀与防护,2011,32(7):525-527.
WANG Y, LIU G Y. Corrosion resistance of 5A01 aluminum alloy plate for marine[J]. Corrosionand Protection,2011,32(7):525-527. (in Chinese)
[15] CHEN R Y, CHU H Y, LAI C C, et al. Effects of annealing temperature on the mechanical properties and sensitization of 5083-H116 aluminum alloy[J]. Proceedings of the Institution of Mechanical Engineers, Part L: Journal of Meterials: Design and Applications, 2015, 229(4):339-346.
[16] 孟凡林,周崇.冷变形及退火对船用5083铝合金板腐蚀性能的影响[J].轻合金加工技术,2015,43(10):35-39,52.
MENG F L, ZHOU C. Effect of cold deformation and annealing on corrosion property of 5083 aluminum alloy marine sheet[J].Light Alloy Fabrication Technology,2015,43(10):35-39,52. (in Chinese)
[17] MA Q B, ZHANG D, ZHUANG L Z, et al. Intergranular corrosion resistance of Zn modified 5XXX series Al alloy during retrogression and re-aging treatment[J]. Materials Characterization, 2018, 144:264-273.
[18] MENG G, LI B L, LI H M, et al. Hot deformation behavior of an Al-5.7wt.%Mg alloy with erbium[J]. Materials Science & Engineering A, 2009, 516(1/2):131-137.
[19] LIN S P, NIE Z R, HUANG H, et al. Annealing behavior of a modified 5083 aluminum alloy[J]. Materials & Design, 2010, 31(3):1607-1612.
[20] DING Y S, GAO K Y, HUANG H, et al. Nucleation and evolution of β phase and corresponding intergranular corrosion transition at 100-230 ℃ in 5083 alloy containing Er and Zr[J]. Materials & Design,2019,174:107778.
[21] DING Y S, WU X L, GAO K Y, et al. The influence of stabilization treatment on long-term corrosion resistance and microstructure in Er and Zr containing 5083 aluminum alloy[J]. Materials Characterization,2020,161:110143.
[22] JONES R H, BAER D R, DANIELSON M J, et al. Role of Mg in the stress corrosion cracking of an Al-Mg alloy[J]. Metallurgical and Materials Transactions A, 2001,32(7):1699-1711.
[23] MILJANA P, ENDRE R. Characterization of microstructural changes in an Al-6.8wt.% Mg alloy by electrical resistivity measurements[J]. Materials Science and Engineering,2008,
492(1/2): 460-467.
[24] 汪永红,李成华,鄂孔元,等.热处理工艺对5083铝合金船用板晶间腐蚀的影响[J].重庆文理学院学报(社会科学版),2013,32(5):8-12.
WANG Y H, LI C H, E K Y, et al. Effect of heat treatment on intergranular corrosion of 5083 aluminum alloy sheet[J]. Journal of Chongqing University of Arts and Sciences (Social Sciences Edition),2013,32(5):8-12. (in Chinese)
[25] 刘国元.晶间腐蚀评价标准ASTM G67国内试验条件适应性研究[J].热加工工艺,2014,43(12):90-91.
LIU G Y. Study on domestic test application of intergranular corrosion evaluation standard ASTM G67[J]. Hot Working Techno-logy,2014,43(12):90-91.(in Chinese)
[26] 杨鸿驰,陆科呈,刘俊生,等.硝酸含量对5083-H116铝合金板材晶间腐蚀的影响[J].腐蚀与防护,2018,39(2):122-123,128.
YANG H C, LU K C, LIU J S, et al. Effect of nitric acid concentration on intergranular corrosion of 5083-H116 aluminum alloy plates[J]. Corrosion and Protection,2018,39(2):122-123,128. (in Chinese)
[27] 罗兵辉,单毅敏,柏振海.退火温度对淬火后冷轧5083铝合金组织及腐蚀性能的影响[J].中南大学学报(自然科学版),2007,38(5):802-808.
LUO B H, SHAN Y M, BO Z H. Effect of annealing temperature on microstructure and corrosive properties of cold-rolled 5083 aluminum alloy after quenching[J]. Journal of Central South University (Science and Technology),2007,38(5):802-808. (in Chinese)

[1]	王磊, 徐超, 李淼, 赵慧武. 多飞行器协同任务分配的改进粒子群优化算法[J]. 兵工学报, 2023, 44(8): 2224-2232.
[2]	李烨, 郑纯, 马长胜, 邱荣贤. 基于拦截效率最大化的高功率微波武器系统与中近程防空武器协同作战目标分配模型[J]. 兵工学报, 2023, 44(11): 3489-3497.
[3]	叶海潮，范武林，秦国华，林锋，郑许，杨扬. 基于翘曲度阈值约束的铝合金板材热轧工艺优化与实验验证[J]. 兵工学报, 2020, 41(8): 1623-1632.
[4]	高飞，潘长明，孙磊. Bayes匹配场地声参数反演:多步退火Gibbs采样算法[J]. 兵工学报, 2017, 38(7): 1385-1394.
[5]	张雪辉，谢臣珍，李晓闲，刘位江，杨凯，蒋苗，祝绳健. Al₂O₃-弥散强化铜合金的退火行为研究[J]. 兵工学报, 2017, 38(11): 2220-2225.
[6]	孙玉山，李岳明，张英浩，万磊. 改进的模拟退火算法在水下机器人S面运动控制参数优化中的应用[J]. 兵工学报, 2013, 34(11): 1418-1423.