内爆炸载荷下弹钢的动态变形与断製准则研究

兵工学报 ›› 1996, Vol. 17 ›› Issue (1): 88-92.

内爆炸载荷下弹钢的动态变形与断製准则研究

隋树元、王淼勋、马晓青、周兰庭

北京理工大学，北京，100081

收稿日期:1995-12-01 修回日期:2012-09-16 上线日期:2014-12-25
通讯作者: 隋树元

A Study on the Dynamic Deformation and Fracture Criterion of Shell Steels Explosive Loaded Internally

Sui Shuyuan, Wang Miaoxun, Ma Xiaoqing, et al.

Beijing Institute of Technology, Beijing, 100081

Received:1995-12-01 Revised:2012-09-16 Online:2014-12-25
Contact: Sui Shuyuan

摘要/Abstract

摘要： 在Taylor临界应力断裂准则的基础上，假定裂纹前端周向拉伸应力σθ= kσB，理论和实验研究了两糟弹钢（20#钢和9260钢）在内爆炸载荷作用下壳体的膨胀规律，以及断裂系数耳值，应交，应交率和破裂半径。破片回收试验表明，理论计算与实验结果具有相当好的一致性。

关键词: 断裂准则 , 断裂系数 , 破裂半径 , 高应变率

Abstract: On the basis of Taylor's tensile stress fracture criterion, and assuming that the tangential tensile stress σθ= KσΒ at the crack’s tip, the radial expansion, fracture co?efficient k，stress-strain, strain rate and burst radius of 2 varieties of shell steel are studied both in theory and experimentally. Fragments collected in the tests show that theoretical calculations are in good agreement with experimental results.

Key words: fracture criterion , fracture coefficient , burst radius , high strain rate

隋树元、王淼勋、马晓青、周兰庭. 内爆炸载荷下弹钢的动态变形与断製准则研究[J]. 兵工学报, 1996, 17(1): 88-92.

Sui Shuyuan, Wang Miaoxun, Ma Xiaoqing, et al.. A Study on the Dynamic Deformation and Fracture Criterion of Shell Steels Explosive Loaded Internally[J]. Acta Armamentarii, 1996, 17(1): 88-92.

[1]	王凡, 郭伟国, 吴倩, 高猛. 高应变率下高温应变计灵敏度系数的校准方法[J]. 兵工学报, 2022, 43(4): 899-909.
[2]	朱建军，李伟兵，李文彬，王晓鸣，郑宇，卢海涛，袁书强. 高应变率下金属柱壳动态变形及形成破片特性研究[J]. 兵工学报, 2017, 38(10): 1933-1941.
[3]	王永刚，徐东明. 高应变率下延性金属中微孔洞贯通行为的数值分析[J]. 兵工学报, 2012, 33(9): 1095-1100.
[4]	索涛，李玉龙，刘明爽. 二维C/SiC复合材料高温压缩力学行为研究[J]. 兵工学报, 2010, 31(4): 516-520.
[5]	隋树元、周兰庭、马晓青、王淼勋. 榴弹弹钢动态特性的实验研究[J]. 兵工学报, 1995, 16(3): 93-96.
[6]	1:杨道明、于捷、李紫桐;2:段祝平. 高应变率下三种钢材性能及损伤机理的实验研究[J]. 兵工学报, 1992, 13(3): 65-73.