“外嵌内包”微结构的奥克托今/铝复合粒子制备及其应用性能

doi:10.3969/j.issn.1000-1093.2021.08.007

摘要/Abstract

摘要： 为改善铝粉在炸药爆轰过程中的动力学条件，采用喷雾包覆法制备奥克托今/铝（HMX/Al）复合粒子，并基于该粒子制备含铝炸药，利用扫描电镜、能谱仪和红外光谱分别对HMX/Al复合粒子形貌、表面元素组成以及化学结构进行表征；通过机械感度、爆热、金属驱动和爆炸罐试验，研究HMX/Al复合粒子基含铝炸药的爆炸性能。结果表明：粒径为13 μm、未经酯类物质清洗及无氟橡胶2603（F2603）预包覆的铝粉有利于形成“外嵌内包”的微结构；HMX/Al复合粒子通过非键作用形成复合结构；制备工艺对撞击感度无显著影响，“外嵌内包”微结构可将HMX/Al复合粒子的摩擦感度由88%降低至12%；HMX/Al复合粒子基含铝炸药的爆热、驱动金属飞片的最大速度和后燃最高温度比传统含铝炸药分别提高5.5%、7.3%和6.4%，证明HMX/Al复合粒子可以使铝粉提前参与爆轰反应，提高铝粉反应完全性。

关键词: 奥克托今/铝复合粒子, 喷雾包覆法, 微结构, 铝粉反应完全性

Abstract: In order to improve kinetics conditions of aluminum during detonation, HMX/Al composite particles were prepared by spray coating method, and aluminized explosives containing the particles were prepared. The morphologies and surface element composition of composite particles were characterized by scanning electron microscopy (SEM) and energy dispersive spectrum (EDS), and the chemistry structure was analyzed by infrared spectroscopy (IR). Explosion performance of HMX/Al composite-based aluminized explosive were estimated through the test of mechanical sensitivity, detonation heat, metal driving and explosion chamber. Results show that the optimized preparation conditions of “surface embedded and inner coated” microstructure are powdered aluminum with particle size of 13 μm without F2603 pre-coating and ester pre-cleaning. The connection of composite particles between HMX and Al is formed by non-bonding. The preparation process has no significant effect on impact sensitivity of composite particles, while the friction sensitivity of HMX/Al composite particles with “surface embedded and inner coated” microstructure is significantly reduced from 88% to 12%. Detonation heat, maximum speed of metal-driving flyer and afterburning maximum temperature of composite particles-based aluminized explosives are 5.5%, 7.3% and 6.4% higher than those of traditional samples, respectively. This indicates that the HMX/Al composite particles can be used to make the aluminum powder participate in detonation reaction in advance and improve its reaction completeness.

Key words: HMX/Alcompositeparticle, spraycoatingmethod, microstructure, reactioncompletenessofpowderedaluminum

中图分类号:

TQ564.3
TJ55

冯晓军，薛乐星，冯博，潘文. “外嵌内包”微结构的奥克托今/铝复合粒子制备及其应用性能[J]. 兵工学报, 2021, 42(8): 1631-1637.

FENG Xiaojun， XUE Lexing， FENG Bo， PAN Wen. Preparation of HMX/Al Composite Particles with “Surface Embedded and Inner Coated” Microstructure bySpray Coating and Its Applied Performance[J]. Acta Armamentarii, 2021, 42(8): 1631-1637.

参考文献

［1］ ZHI J, LI S F, ZHAO F Q, et al. Thermal behavior of HMX and metal powders of different grade[J]. Journal of Energetic Materials, 2002, 20(2):165-173.
[2] 陈朗, 张寿齐, 赵玉华. 不同铝粉尺寸含铝炸药加速金属能力的研究[J].爆炸与冲击, 1999, 19(3):250-256.
CHEN L, ZHANG S Q, ZHAO Y H. Study of the metal acceleration capacities of aluminized explosives with spherical aluminum particles of different diameter[J]. Explosion and Shock Waves, 1999,19(3):250-256. (in Chinese)
[3] JAYARAMAN K, ANAND K V, BHATT D S, et al. Production, characterization, and combustion of nanoaluminum in composite solid propellants[J]. Journal of Propulsion and Power, 2009, 25(2): 471-481.
[4] YE M Q,ZHANG S T, LIU S S, et al. Preparation and characterization of pyrotechnics binder-coated nano-aluminum composite particles[J]. Journal of Energetic Materials, 2017, 35(3): 300-313.
[5] LI Y R, REN H, YAN T, et al. Reactivity of fluororubber-modified aluminum in terms of heat transfer effect[J]. Journal of Thermal Analysis and Calorimetry, 2020, 142(2): 871-876.
[6] 闫涛, 任慧, 马爱娥, 等. 氟橡胶包覆层对纳米铝粉性能的影响研究[J]. 兵工学报, 2019, 40(8):1611-1617.
YAN T, REN H, MA A E, et al. Effect of fluororubber coating on the properties of nano-aluminum powders[J]. Acta Armamentarii, 2019, 40(8):1611-1617. (in Chinese)
[7] 王慧心, 任慧, 闫涛, 等. 聚乙烯醇原位包覆铝粉结构表征及活性铝含铝测定[J]. 兵工学报, 2019, 40(7): 1373-1380.
WANG H X, REN H, YAN T, et al. Micro-structure and active aluminum content of aluminum power in situ coated by polyvinyl alcohol[J].Acta Armamentarii, 2019, 40(7): 1373-1380. (in Chinese)
[8] HWANG J S, KIM C K, CHO W H, et al. Development of new thermobaric explosive composition using nickel coated aluminum powder[C]∥Proceedings of 38th International Annual Conference of ICT. Karlsruhe, German：ICT, 2008.
[9] ANDERSON P, BALAS W, NICOLICH S, et al. Development, optimization, and application of combined effects explosives[C]∥Proceedings of 2009 Insensitive Munitions & Energetic Materials Technology Symposium. Tucson, AZ, US: NDIA, 2009.
[10] SEHOENITZ M, WARD T S, DREIZIN E L. Fully dense nano-composite energetic powders prepared by arrested reactive milling[J]. Proceedings of the Combustion Institute, 2005, 30(2): 2071-2078．
[11] SEHOENITZ M, WARD T S, DREIZIN E L. Preparation of energetic metastable nano-composite materials by arrested reactive milling[C]∥Proceedings of Synthesis, Characterization and Properties of Energetic/Reactive Nanomaterials Symposium. Warrendale, PA, US: Materials Research Society, 2004．
[12] ELBASUNEY S, EL-SAYYAD G S, ISMAEL S, et al. Colloid thermite nanostructure: a novel high energy density material for enhanced explosive performance[J]. Journal of Inorganic and Organometallic Polymers and Materials, 2021, 31(6):559-565.
[13] YANG H, LIU Y, HUANG H, et al. Preparation and characterization of the Al/Fe₂O₃/RDX/NC nanocomposites by electrospray[J]. Journal of Thermal Analysis and Calorimetry, 2019,137(5): 1615-1620.
[14] ZHIGACH A N, LEIPUNSKII I O, PIVKINA A N, et al. Aluminum/HMX nanocomposites: synthesis, microstructure, and combustion[J]. Combustion, Explosion, and Shock Waves, 2015, 51(1):100-106.
[15] 孙业斌, 惠君明, 曹欣茂. 军用混合炸药[M]. 北京: 兵器工业出版社, 1995: 385-389.
SUN Y B, HUI J M, CAO X M. Military mixed explosive[M]. Beijing: Publishing House of Ordnance Industry, 1995: 385-389. (in Chinese)

第42卷第8期2021 年8月
兵工学报ACTA ARMAMENTARII
Vol.42No.8Aug.2021

[1]	查明霞，马振叶，徐娟，秦红，徐司雨，赵凤起. 液相化学法制备纳米铝粉及其表征[J]. 兵工学报, 2014, 35(10): 1575-1580.
[2]	王建华, 刘瑶, 闫利伟, 刘玉存, 常双君, 于雁武. 集成器件化纳微结构炸药片制备及性能研究[J]. 兵工学报, 2013, 34(8): 953-957.
[3]	侯朝霞，苏春辉，张华山，张洪波. 锌铝硅系透明玻璃陶瓷晶化行为研究[J]. 兵工学报, 2007, 28(2): 253-256.