双乳液法制备微孔球形药的孔结构形成机制

doi:10.3969/j.issn.1000-1093.2016.09.012

摘要/Abstract

摘要： 为了揭示双乳液法制备微孔球形药孔结构的形成机制，分别在乳化、成球及溶剂蒸馏等过程中进行取样，并采用显微观察和图像分析方法探索了孔结构的形成和演变规律。结果表明：影响微孔球形药中孔结构形成的主要因素是乳化条件和溶剂蒸馏条件。硝化棉乳液中分散相水滴的形态及尺寸分布规律与成品微孔球形药中的孔结构及孔径分布规律基本一致。乳化条件决定球形药中孔的形貌特征；成球过程的工艺条件对孔径及孔的形貌无显著影响；溶剂蒸馏条件对孔径分布影响较大，溶剂蒸馏速度加快，孔隙发生聚集而导致孔径分布不均匀。通过降低溶剂蒸馏速度，成品颗粒中的孔结构均匀性可以得到有效改善。采用双乳液法制备的硝化棉基微孔球形药中的孔结构是由硝化棉乳液中的分散相液滴形态决定的。

关键词: 兵器科学与技术, 含能材料, 双乳液法, 微孔, 球形药, 孔结构, 形成机制

Abstract: The formation mechanism of pore structure of ball propellant with micro-pores made by double emulsion method is revealed. The formation and changing rule of pore structure are studied through sampling, microscopic observation and image analysis during emulsifying, balling and solvent distilling. The results show that the major parameters influencing the shape forming of pore structure are the conditions of emulsion and solvent distillation. The shape and size distribution of dispersed droplets in nitrocellulose emulsion are in basic agreement with the pore structure and pore size distribution in finished ball propellant. As a result, the pore morphology of ball propellant is determined by the emulsification conditions. The conditions of shape forming process have no significant effect on the size and morphology of the pores, while the solvent evaporation conditions have greater influence on the pore size distribution. The faster the solvent is distilled, the worse the pore structure uniformity is due to the agglomeration of pores. The pore structure uniformity of finished particles is improved effectively by reducing the speed of solvent distillation. The pore structure of nitrocellulose ball propellant with micro-pores made by double emulsion method is substantially determined by the morphology of the disperse phase droplets in nitrocellulose emulsion.

Key words: ordnance science and technology, energetic material, double emulsion method, micro-pore, ball propellant, pore structure, formation mechanism

中图分类号:

TQ562⁺.21

蔺向阳，李翰，郑文芳, 潘仁明. 双乳液法制备微孔球形药的孔结构形成机制[J]. 兵工学报, 2016, 37(9): 1633-1638.

LIN Xiang-yang, LI Han, ZHENG Wen-fang, PAN Ren-ming. Formation Mechanism of Pore Structure of Ball Propellant with Micro-pores Made by Double Emulsion Method[J]. Acta Armamentarii, 2016, 37(9): 1633-1638.

参考文献

［1］ Fischer T S, Messmer A. Burning characteristics of foamed polymer bonded propellants[C]∥19th International Symposium on Ballistics. Interlaken, Switzerland: International Ballistics Society, 2001: 107-114.
[2］ Bhnlein-Mau β J，Krber H. Technology of foamed propellants[J]. Propellants Explosives and Pyrotechnics, 2009, 34(3): 239-244.
[3］陈西如，应三九，肖正刚. 超临界CO₂制备微孔球扁药的研究[J].兵工学报，2012，33（5）：534-539.
CHEN Xi-ru，YING San-jiu，XIAO Zheng-gang. Research on preparation of microfoam oblate spherical propellants by supercritical CO₂[J]. Acta Armamentarii, 2012，33（5）：534-539.(in Chinese)
[4］应三九，徐复铭. 发射药超临界发泡微孔制备技术研究[J].兵工学报，2013，34（10）：261-268.
YING San-jiu，XU Fu-ming. Research on supercritical fluid foaming technology for preparation of microcellular foamed propellants[J]. Acta Armamentarii, 2013，34(10): 261-268.(in Chinese)
[5］ Li Y X, Yang W T, Ying S J. Investigation on the foaming behaviors of NC-based gun propellants[J]. Defence Technology, 2014, 10(3):261-268.
[6] Kim H K, Chung H J, Park T G. Biodegradable polymeric microspheres with “open/closed” pores for sustained release of human growth hormone[J]. Journal of Controlled Release, 2006, 112(2): 167-174.
[7］ Gokmen M T, Prez F E D. Porous polymer particles—a comprehensive guide to synthesis, characterization, functionalization and applications[J]. Progress in Polymer Science, 2012, 37(3):365-405.
[8] Kiss N, Brenn G, Suzzi D,et al. The influence of process parameters on the properties of PLGA-microparticles produced by the emulsion extraction method[J]. American Institute of Chemical Engineers, 2013, 59(6): 1868-1881.
[9] Wang J C, Dong X Y. Preparation and characterization of ethyl menthane carboxamide microcapsules using PLA[J]. Journal of Applied Polymer Science, 2013, 129(2): 665-671.
[10] Fu J, Wang D X, Wang T, et al. High entrapment efficiency of chitosan/polylactic acid/tripolyphotspate nanosized microcapsules for rapamycin by an emulsion-evaporation approach[J]. Journal of Biomedical Nanotechnology, 2010, 6(6): 725-728.
[11］ Giri T K, Choudhary C, Ajazuddin, et al. Prospects of pharmaceuticals and biopharmaceuticals loaded microparticles prepared by double emulsion technique for controlled delivery[J]. Saudi Pharmaceutical Journal, 2013, 21(2):125-41.
[12］ Nair M, Lusignan1 C P, Boris D C. Preparation of uniform micrometer-sized polymer particles with closed-cell porous architecture made by limited coalescence of a double emulsion[J]. Colloids and Surfaces A: Physicochemical and Engineering Aspects, 2014, 443(4): 583-595.
[13］蔺向阳,刘玉军,殷继刚,等. 微气孔球形药的定容燃烧性能[J].火炸药学报, 2011, 34（6）: 80-83.
LIN Xiang-yang, LIU Yu-jun, YIN Ji-gang, et al. Combustion characteristics of ball powder with micropores[J]. Chinese Journal of Explosives & Propellants, 2011, 34(6): 80-83. (in Chinese)
[14］蔺向阳, 程向前, 潘仁明, 等. 微气孔球形药常压燃烧特征[J]. 火炸药学报, 2005, 28（4）: 68-71.
LIN Xiang-yang, CHENG Xiang-qian, PAN Ren-ming, et al. Combustion property of oblate propellant with micropore in air[J]. Chinese Journal of Explosives & Propellants，2005, 28(4): 68-71. (in Chinese)
［15］王萍, 张磊, 蔺向阳, 等. 溶剂浸析法制备硝化棉基微孔球形药［J］. 含能材料, 2015, 23（3）：1107-1110.
WANG Ping, ZHANG Lei, LIN Xiang-yang, et al. Preparation of nitrocellulose-based micro-pores spherical powder by solvent leaching method［J］. Chinese Journal of Energetic Materials,2015, 23（3）：1107-1110. (in Chinese)
[16］蔺向阳, 刘玉军, 殷继刚, 等．微气孔球形药常压传火速度的测试方法[J]．火炸药学报, 2010, 33（3）：72-75, 83.
LIN Xiang-yang, LIU Yu-jun, YIN Ji-gang, et al. Flame spread speed test method of ball powder with micropores at normal pressure[J]. Chinese Journal of Explosives & Propellants, 2010, 33(3): 72- 75, 83. (in Chinese)
[17］蔺向阳, 段红珍, 潘仁明, 等．单基微气孔球扁药的静电感度研究[J]．含能材料，2008，16（1）：83-85．
LIN Xiang-yang, DUAN Hong-zhen, PAN Ren-ming, et al. Electrostatic spark sensitivity of single base oblate propellant with micropores[J]. Chinese Journal of Energetic Materials, 2008，16(1): 83-85. (in Chinese)
[18］蔺向阳，刘玉军，石上，等. 微孔型无烟烟花发射药装药技术[J]. 南京理工大学学报，2011，35（4）：552-557.
LIN Xiang-yang, LIU Yu-jun, SHI Shang, et al. Study on charging technology of micropores smokeless propellant for firework [J]. Journal of Nanjing University of Science and Technology，2011, 35(4)：552-557.(in Chinese)

[1]	蔡尚晔，姜春兰，毛亮，王在成，胡榕，叶胜. 含孔隙富铝聚四氟乙烯/铝含能材料冲击温升规律[J]. 兵工学报, 2021, 42(2): 225-233.
[2]	肖磊, 王庆华, 李万辉, 刘巧娥, 郝嘎子, 高向东, 柯香, 刘杰, 姜炜, 乔羽, 谭诚. 基于三维打印技术的纳米奥克托今与梯恩梯熔铸炸药制备及性能研究[J]. 兵工学报, 2018, 39(7): 1291-1298.
[3]	牟科赛，古勇军，蔺向阳，郑文芳，潘仁明. 水溶性氧化剂在微孔球形药中原位超细化分散方法研究[J]. 兵工学报, 2018, 39(10): 1958-1964.
[4]	娄伟鹏，郑长松，李和言，陈建文，张周立，马源. 高速《Symbol》v湿式换挡离合器排油阀临界开启和关闭压力研究[J]. 兵工学报, 2017, 38(9): 1665-1672.
[5]	王宪成，杨绍卿，马宁，赵文柱. 车辆柴油机缸套动载荷磨损计算模型研究[J]. 兵工学报, 2017, 38(9): 1673-1680.
[6]	孙皓泽，常天庆，王全东，孔德鹏，戴文君. 一种基于分层多尺度卷积特征提取的坦克装甲目标图像检测方法[J]. 兵工学报, 2017, 38(9): 1681-1691.
[7]	张玉燕，孙莎莎，王振春，曹海要，战再吉. 高速载流电枢表面瞬态温度场仿真与测量[J]. 兵工学报, 2017, 38(9): 1692-1698.
[8]	李臣明，宦超，石怀龙. 某箱式火箭炮对面目标分布式杀伤最优火力分配[J]. 兵工学报, 2017, 38(9): 1699-1704.
[9]	雷娟棉，张嘉炜，谭朝明. 小攻角下船尾外形对旋转弹丸马格努斯效应影响的数值研究[J]. 兵工学报, 2017, 38(9): 1705-1715.
[10]	李泽，闫晓鹏，栗苹，郝新红，王建涛. 扫频式干扰对调频多普勒引信的干扰机理研究[J]. 兵工学报, 2017, 38(9): 1716-1722.
[11]	张浩为，谢军伟，张昭建，宗彬锋，陈唐军. 基于混合自适应遗传算法的相控阵雷达任务调度[J]. 兵工学报, 2017, 38(9): 1761-1770.
[12]	李茂，侯海量，朱锡，黄晓明，李典，陈长海，胡年明. 结构间隙对芳纶纤维增强复合装甲结构抗侵彻性能的影响[J]. 兵工学报, 2017, 38(9): 1797-1805.
[13]	王鉴, 韩焱, 王黎明, 张丕状, 陈平. 弹丸在膛内运动的回波信号瞬时频率估计方法研究[J]. 兵工学报, 2017, 38(9): 1806-1814.
[14]	刘海鸥，张文胜，徐宜，赵梓烨. 基于核密度估计的履带车辆传动轴载荷谱编制[J]. 兵工学报, 2017, 38(9): 1830-1838.
[15]	姜缪文，闫健卓，陈继民. 基于拓扑优化技术的军用头盔内胆结构三维打印[J]. 兵工学报, 2017, 38(9): 1845-1853.